Influencia do teor de carbono na propagação de trinca por fadiga e na tenacidade a fratura em camada cementada em aços de alta resistencia mecanica / Influence of the carbon content on propagation in cracks of fadigue and on fracture toughness in carburized case in high strenght steels

Orientador: Itamar Ferreira / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-10T13:08:50Z (GMT). No. of bitstreams: 1
Sandor_LeonardoTaborda_D.pdf: 12861330 bytes, checksum: 648e60efeced3118f4ec8272c46bddcc (MD5)
Previous issue date: 2008 / Resumo: Este trabalho propõe uma metodologia para avaliar pontualmente as variações de tenacidade à fratura e taxa de crescimento de trinca de fadiga ao longo da camada cementada de um aço SAE 4320. A pequena espessura dessas camadas impede a retirada de corpos de prova nas dimensões especificadas pelas normas de ensaios de tenacidade à fratura. Assim, para simular uma camada cementada retirou-se amostras de aços SAE 43xx variando-se apenas teor de carbono de 0,20 a 1,00%. Os corpos de prova após eletrodeposição de cobre foram tratados termicamente numa carga de cementação, têmpera e revenimento para serem submetidos aos efeitos térmicos sem absorção de carbono. Os resultados da análise microestrutural, dos ensaios de microdureza, de tração e de tenacidade à fratura e de taxa de crescimento de trinca de fadiga foram agrupados em um único gráfico e comparados com o perfil de cementação de peças de aço SAE 4320 tratadas nas mesmas condições. Foi confirmado que as propriedades de fadiga variam de forma inversamente proporcional à microdureza (HV1) e que a previsão do comportamento de uma trinca numa camada cementada pode ser feita por meio de equação ou diagrama que relacionam a microdureza HV1 com a tenacidade à fratura ou taxa de crescimento de trinca de fadiga (KIC ou da/dN x ??) / Abstract: The purpose of this work is to propose a methodology for evaluating the crack growth rate and the fracture toughness along the SAE 4320 steel carburized layer. Due to the small thickness of those layers, it is impossible to machine specimens from those layers in accordance with standards. For simulating the microstructures of the carburized layer in order to get samples for tensile and the fracture toughness testing, specimens of SAE 43xx, from 0.20 %C to 1.00 %C, steels melted in vacuum induction melting, hot rolled and have been machined, assuming the local influence just the variation of the content of carbon and considering that the contents of the other alloy elements are essentially constant. The specimens after electroplated copper layer were heat treated in an industrial load of carburizing, quenching, and tempering for they be submitted to the thermal effects without absorption of carbon. The results of the microstructure analysis and microhardness, crack growth rate, and the fracture toughness tests were placed in a single graph
and compared with the profile of the carburizing of the steel SAE 4320 heat treated in the same conditions. It was confirmed that the crack growth rate and the fracture toughness varies inversely proportional to the microhardness (HV1) and that the forecast of the behavior of a crack in a carburized layer can be made through equation or it designs that relate the microhardness (HV1) with the fracture toughness (KIC or CTODC) and crack growth rate (da/dN X ??) / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264857
Date01 October 2008
CreatorsSandor, Leonardo Taborda
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Ferreira, Itamar, 1952-, Spinelli, Dirceu, Gallego, Juno, Button, Sergio Tonini, Santos, Rezende Gomes dos
Publisher[s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Format202p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds