This diploma thesis builds on my bachelor thesis, which was focused on the application of low-pressure hydrogen plasma and argon-hydrogen plasma on layers of corrosion products. According to results of the experiments, an appropriate temperature for plasma chemical treatment of lead samples was detected. However, the process of corrosion removal through plasma chemical treatment needs to be further optimized to prevent potential damage to the original historical artefacts. Optimization of the treatment process is therefore the main subject of this work’s research. The model samples with artificial corrosion layers with dual composition were prepared. These samples were put to desiccator with sand and organic acid. The samples corroded in environment of acetic acid or formic acid with the aim of creating the corrosion, which would be at least partially simulated with corrosion on the original artefacts. The process of corrosion lasted for eleven months. After that, the samples were dried out under reduced pressure, put to the protecting foil with humid and oxygen absorbers. In contrast with my bachelor thesis where the continuous regime was chosen for the treatment, the pulse regime with three different condition settings is used. Process of experiment was monitored by OES, surface of samples was analyzed by SEM, EDX, XRD methods. Results from experiments with model samples were used for treatment of original artefacts with missing documentation, so their eventual damaging was acceptable.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:449329 |
Date | January 2021 |
Creators | Bubnová, Kateřina |
Contributors | Grossmannová, Hana, Krčma, František |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0013 seconds