Orientador: Amauri Garcia / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-09T07:59:55Z (GMT). No. of bitstreams: 1
Rosa_DanielMonteiro_D.pdf: 8184541 bytes, checksum: 0b8d932ad9a1091a507ea6b10e4185f8 (MD5)
Previous issue date: 2007 / Resumo: As morfologias das estruturas de solidificação, caracterizadas principalmente por arranjos celulares e dendríticos, e suas grandezas representadas por espaçamentos celulares e dendríticos primários, secundários e terciários, controlam os perfis de segregação e a formação de segundas fases dentro das regiões intercelulares ou interdendríticas, que determinam as propriedades finais das estruturas fundidas. O presente trabalho pretende contribuir para o entendimento do desenvolvimento microestrutural de ligas binárias através da análise de dois sistemas binários que possuem elevada importância para a indústria na fabricação de peças fundidas automotivas e grades de baterias: Al-Si e Pb-Sb, respectivamente. Os experimentos realizados utilizaram dois diferentes dispositivos em que o calor é extraído somente pelo sistema de resfriamento a água, localizado no fundo (solidificação ascendente) e no topo (solidificação descendente) da lingoteira. As variáveis térmicas de solidificação foram determinadas pela leitura de temperaturas a partir de termopares posicionados dentro da lingoteira em diferentes posições em relação à superfície refrigerada. Estas variáveis térmicas foram confrontadas com as previsões teóricas de um modelo numérico de solidificação. Os aspectos macroestruturais e microestruturais foram caracterizados ao longo dos lingotes através de microscopia óptica. Para as ligas Al-Si foi realizada uma análise complementar do efeito da convecção térmica e constitucional nos espaçamentos dendríticos terciários na solidificação unidirecional transitória descendente. Ligas hipoeutéticas Pb-Sb foram utilizadas para analisar as influências das variáveis térmicas de solidificação e da concentração de soluto nas estruturas celulares, na transição celular/dendrítica e nas estruturas dendríticas. Os espaçamentos celulares e dendríticos foram comparados com as previsões teóricas fornecidas pelos principais modelos de crescimento estacionário e transitório da literatura. Foram também examinados os efeitos da taxa de resfriamento no crescimento celular da liga Pb 0,85%Sb e a influência do tamanho celular e do perfil de macrossegregação correspondente na resistência à corrosão / Abstract: The morphologies of as-cast microstructures, characterized mainly by cellular and dendritic patterns, and their scales represented by primary, secondary and tertiary arm spacings, control the segregation profiles and the formation of secondary phases within intercellular and interdendritic regions, which determine the final properties of castings. The present work aims to contribute to the understanding of microstructural development of binary alloys by analyzing two binary systems, which possess high industrial importance in the manufacture of as-cast automotive components and battery grids: Al-Si and Pb-Sb, respectively. Experiments have been carried out by using two castings assemblies, which were designed in such way that heat was extracted only through the water-cooled system, located at the bottom (upward solidification) and at the top (downward solidification) of the casting. The solidification thermal variables have been determined from thermal readings acquired by thermocouples located inside of the casting in different positions from the cooled surface. Such experimental thermal variables have been compared with theoretical predictions of a numerical model of solidification. Macrostructural and microstructural aspects along the casting were characterized by optical microscopy. For Al-Si alloys a complementary analysis of the influence of thermosolutal convection on the tertiary dendrite arm spacing during the downward unsteady-state directional solidification has been carried out. Hypoeutectic Pb-Sb alloys have been used to analyze the influences of solute concentrations and solidification thermal variables in the development of cellular structures, the cellular/dendritic transition and dendritic structures. Experimental cellular and dendritic spacings have been compared with the theoretical predictions furnished by the main steady-state and unsteady-state growth models from the literature. The effect of cooling rate on the cellular growth of a Pb 0.85wt%Sb alloy and the influences of cell size and of the corresponding macrosegregation profile on the resultant corrosion behavior have also been examined. / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/264735 |
| Date | 31 May 2007 |
| Creators | Rosa, Daniel Monteiro |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Garcia, Amauri, 1949-, Ierardi, Maria Clara Filippini, Freire, Celia Marina de Alvarenga |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 171p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds