The purpose of the thesis is to investigate the improvement of single-crystal Si solar cell efficiency using porous Indium tin oxide (ITO)/ITO double layer antireflection(AR) coating. The resistivity, transmittance and refraction index of the porous ITO films prepared by supercritical CO2 treatment were investigated. At a 2000 psi pressure and 60¡CC, the resistivity of porous ITO films is 15 £[-cm, the average transmittance is better than 95 %, and the refraction index is 1.54. In addition, the resistivity of ITO thin films fabricated by reactive ratio-frequency magnetron sputtering is 7¡Ñ10-4 £[-cm, the average transmittance are 85 %, and the refraction index is 2.0.
For the single crystal-Si solar cell with porous ITO/ITO double layer AR coating, the open circuit voltage, short circuit current, fill factor and efficiency are measured.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0706111-164600 |
| Date | 06 July 2011 |
| Creators | Wu, Shih-Chieh |
| Contributors | Jing-Yuan Lin, Chao-Kuei Lee, Fang-Zheng Lin, Yi-Jen Chiu, Ann-Kuo Chu |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0706111-164600 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0018 seconds