Previous issue date: 2016-02-26 / Implantes dent?rios s?o suportes ou estruturas de materiais biocompat?veis
posicionados cirurgicamente no osso maxilar, abaixo da gengiva, para substituir
ra?zes dent?rias, assegurando estruturalmente dentes artificiais ap?s a perda da
denti??o. Desenvolveu-se um m?todo de ensaio, em laborat?rio, para analisar a
resposta mec?nica de um parafuso met?lico implantado em um osso maxilar
inanimado de um porco de cerca de doze meses de idade e imerso em um fluido
com tr?s condi??es de pH: ?cido, b?sico e neutro. Uma solicita??o mec?nica de
contato circunferencial c?clico para simular um processo mastigat?rio unidirecional foi
utilizada para investigar a estabilidade dimensional da uni?o parafuso-osso em
fun??o do n?mero de ciclos sob carga. Ap?s os ensaios com a presen?a de solu??o
?cida, b?sica ou neutra, analisou-se a estrutura porosa do osso maxilar su?no bem
como da cabe?a do parafuso submetida ao contato metal-metal atrav?s de MEV e
microan?lise por EDS. Os resultados das solicita??es triboqu?micas da uni?o
parafuso-osso evidenciaram, na cabe?a do parafuso, a ocorr?ncia de desgaste
abrasivo com forma??o de proa com presen?a de debris e, no osso, dano por fratura
fr?gil com a presen?a de microtrincas em meio ? sua porosidade intr?nseca. As taxas
de desgaste por perda m?ssica do parafuso desatarraxado ap?s cada ensaio
demonstraram surpreendentemente serem menores quando resultantes dos ensaios
com solu??o ?cida e b?sica, enquanto foram maiores as taxas de desgaste dos
parafusos ensaiados em meio a uma solu??o neutra. O contato aqueceu em uma
faixa que variou entre 0,50C at? 16,50C acima da temperatura ambiente. Assim,
atribuiu-se ? a??o ?cida do fluido aquecido pelo atrito entre os contatos sobre o
parafuso met?lico a forma??o de uma nanocamada passivada, respons?vel pelo
menor desgaste medido. A velocidade de vibra??o global foi maior durante o running
in, at? 104 ciclos, do que no regime permanente de ensaios, entre 104 e 105 ciclos,
quando o contato j? se configurara como conforme. O NPS[dB], n?vel de press?o
sonora seguiu esta tend?ncia. O pH do fluido continuou ?cido antes e ap?s os
ensaios, embora haja migrado de 2, no in?cio, para 4, no final. Os demais
permaneceram invari?veis. / Dental implants are material supports and structures biocompatible surgically
positioned into the maxillary bone beneath the gums to replace tooth roots, ensuring
structurally teeth substitutes after the loss of teeth. We have developed an approach
in the laboratory to analyze the mechanical response of a metallic screw implanted in
an inanimate jaw bone of a pig about twelve months of age and immersed in a fluid
at three pH conditions: acidic, basic and neutral. A mechanical stress cyclic
circumferential contact to simulate a unidirectional masticatory process was used to
investigate the dimensional stability of the screw-bone junction in the number of
cycles under load. After the tests on the presence of acidic, basic or neutral solution,
it analyzed the porous structure of the pig maxillary bone and screw head subjected
to metal-to-metal contact through MEV and EDS microanalysis. The results of
tribochemical requests the screw-bone junction showed in the screw head, the
occurrence of abrasive wear with bow training with the presence of debris and bone,
damage by brittle fracture in the presence of microcracks in the midst of their inherent
porosity. The wear rates of mass loss of undoing screw after each test showed
surprisingly are lower when resulting from tests with acidic and basic solution, as
were higher wear rates of the tested screws in the middle of a neutral solution. The
contact heated in a band ranging from 0,5oC to 16,5oC above room temperature.
Therefore, attributed to the acid action of the fluid heated by the friction between the
contacts on the metal bolt the formation of a passivated nanolayer responsible for the
lowest measured wear. The overall vibration velocity was higher during the running
in, up to 104 cycles, than in steady-state tests, between 104 and 105 cycles, when the
contact already configures as conformal. SPL [dB] Sound Pressure Level followed
this trend. The pH of the acid fluid continued before and after the test, although there
is migrated from 2 at the beginning, 4 at the end. The rest remained unchanged.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/21873 |
| Date | 26 February 2016 |
| Creators | Pontes, Gracilene dos Santos Aquino |
| Contributors | 10973370491, Aquino, Marcos Silva de, 47426632415, Souza, Juliana Ricardo de, 05844998413, Souza, Roberto Silva de, 44466927472, Medeiros, Jo?o Telesforo N?brega de |
| Publisher | PROGRAMA DE P?S-GRADUA??O EM ENGENHARIA MEC?NICA, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0011 seconds