The sintering behavior to form TiC-Ni-Mo cermet using a nano-size TiC powders was investigated in flowing Argon gas at 1500°C. Nano-sized titanium carbide powders with high purity, high surface area, and low cost were synthesized from carbon coated Ti containing precursors utilizing a patented process. The sintering studies showed that an increase in theoretical density (TD) with increasing molybdenum content. TiC based cermets were characterized using X-ray diffraction (XRD), Vickers hardness, and scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDS). Mechanical properties, electrical conductivity and oxidation resistance results shows potential applications as interconnect for Low/Intermediate Temperature Solid Oxide Fuel Cells (SOFC) and machining tool tips.
| Identifer | oai:union.ndltd.org:siu.edu/oai:opensiuc.lib.siu.edu:theses-2912 |
| Date | 01 May 2016 |
| Creators | Kong, Jia Huey |
| Publisher | OpenSIUC |
| Source Sets | Southern Illinois University Carbondale |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses |
Page generated in 0.0024 seconds