Caracterização microestrutural de duas juntas soldadas em aço ASTM A743 CA6NM por processo TIG

Submitted by Angela Maria de Oliveira (amolivei@uepg.br) on 2019-02-08T11:08:03Z
No. of bitstreams: 2
license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5)
Willian Ricardo.pdf: 8465496 bytes, checksum: a01921f9da37abb9909a79e5b398408c (MD5) / Made available in DSpace on 2019-02-08T11:08:03Z (GMT). No. of bitstreams: 2
license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5)
Willian Ricardo.pdf: 8465496 bytes, checksum: a01921f9da37abb9909a79e5b398408c (MD5)
Previous issue date: 2018-08-24 / Turbinas hidráulicas usadas em usinas hidrelétricas podem apresentar desgastes por cavitação e trincas em sua operação, as quais em alguns casos reparadas por soldagem a arco elétrico, por ser um processo de menor custo em comparação à troca da turbina. O aço inoxidável martensítico A743 grau CA6NM é empregado em serviços que requerem boa resistência mecânica associada a resistência à corrosão, principalmente em equipamento para extração de petróleo nos rotores e componentes de turbinas hidráulicas. Este trabalho tem por escopo analisar a microestrutura formada após processo de soldagem TIG (Tungsten Inert Gas) de um aço ASTM A743 CA6NM, usando material de adição similar, avaliando a presença da estrutura ferrita delta, austenita retida e carbonetos. Variando as espessuras das amostras e parâmetros de soldagem como passe único de soldagem e multipasse, mantendo temperatura de pré-aquecimento e interpasse de150ºC. Estimando a influência dos parâmetros na microestrutura com a dureza dos cordões e da ZTA. Os experimentos revelaram que um único passe de solda é suficiente para a formação de ferrita delta na forma de rede ao longo do cordão de solda e nas regiões expostas a altas temperaturas na zona termicamente afetada (ZTA), assim como o perfil de durezas da seção transversal do cordão de solda apontam durezas que variam desde 344 ± 6 HV para a região fundida, passando por um pico de dureza de 379 ± 4 HV na ZTA e terminando no metal base com 290 ± 5 HV, na solda multipasse a origem das diferentes morfologias de ferrita é múltipla, havendo uma diferença da taxa de resfriamento nos cordões,sendo que entre a base e o topo da solda pode ser percebido acumulo de ferrita delta na região interpasse e no topo do ultimo cordão de solda e a variação de largura da ZTA pelos passes subsequentes, a morfologia da ferrita delta zona termicamente afetada (ZTA) na condição multipasse, assim como o perfil de durezas da seção transversal dos cordões de solda apontam durezas que variam desde 311 ± 24 HV para a região fundida, passando por um pico de dureza de 326 ± 33 HV na ZTA. / Hydraulic turbines used in hydroelectric plants may present wear by cavitation and cracks in their operation, and in some cases repaired by electric arc welding, being a process of lower cost compared to the turbine exchange. A743 grade martensitic stainless steel CA6NM is used in services that require good mechanical resistance associated with corrosion resistance, especially in oil extraction equipment, rotors and hydraulic turbine components. This work aims to analyze the microstructure formed after TIG (Tungsten Inert Gas) welding of an ASTM A743 CA6NM steel, using similar addition material, evaluating the presence of the delta ferrite, retained austenite and carbides structure. By varying the sample thicknesses and welding conditions as single pass welding and multipass, maintaining preheating temperature and interpass of 150ºC. Estimating the influence of the parameters in the microstructure with the hardness of the strands and the ZTA. The experiments revealed that a single soldering pass is sufficient for the formation of delta ferrite in the form of a net along the weld bead and in the regions exposed to high temperatures in the thermally affected zone (ZTA), as well as the hardness profile of the section cross section of the weld beads indicate hardness ranging from 344 ± 6 HV to the molten region, passing through a hardness peak of 379 ± 4 HV in the ZTA and ending in the base metal with 290 ± 5 HV, in the multipass weld the origin of the different In the present study, the ferrite morphologies are multiple, with a difference in the cooling rate in the cords, between the base and the top of the weld it is possible to detect the accumulation of delta ferrite in the interpass region and at the top of the last weld bead and the ZTA The thermally affected zone delta ferrite (ZTA) morphology in the multipass condition, as well as the cross section hardness profile of the weld beads, point to hardnesses that vary from 311 ± 24 HV for the molten region, passing through a hardness peak of 326 ± 33 HV in the ZTA.

Identiferoai:union.ndltd.org:IBICT/oai:tede2.uepg.br:prefix/2728
Date24 August 2018
CreatorsSantos, Willian Ricardo dos
ContributorsHupalo, Marcio Ferreira, Pukasiewicz, Anderson Geraldo Marenda, Cintho, Osvaldo Mitsuyuki, Lourençatto, Luciano Augusto
PublisherUniversidade Estadual de Ponta Grossa, Programa de Pós-Graduação em Engenharia e Ciências de Materiais, UEPG, Brasil, Departamento de Engenharia de Materiais
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UEPG, instname:Universidade Estadual de Ponta Grossa, instacron:UEPG