Orientador: Edison Bittencourt / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Quimica / Made available in DSpace on 2018-07-13T22:43:46Z (GMT). No. of bitstreams: 1
Lopes_ElizabethBorges_M.pdf: 3383889 bytes, checksum: 195b5562dbb01c1feb34750510101917 (MD5)
Previous issue date: 1991 / Resumo: A avaliação dos processos de degradação de polímeros em condições de serviço pode ser similada por envelhecimento natural ou artificial acelerado em laboratório. O sistema em estudo (LMPI-3/2) provém de uma formulação desenvolvida na UNICAMP, em trabalho conjunto com o CPqD-TELEBRÁS. Este material é um composto curável com UV, constituído basicamente dos oligômeros epóxi acrilatado e uretano acrilatado, de monômero reativo e fotoiniciador. Trabalhou-se também com duas resinas comerciais denominadas Nacional (CN) e Importada (CI). Afim de acompanhar o processo degradativo em curto espaço de tempo, e pelo material em questão ser utilizado continuamente em cabos isolados da radiação solar, optou-se por similar o envelhecimento de filmes e fibras revestidas através de exposições isotérmicas à altas temperaturas. Uma importante característica da fibra de vidro é a sua tendência a enfraquecer sob influência combinada de vapor d¿água e carga aplicada. Assim, em paralelo, tentou-se avaliar o efeito da umidade à partir do condicionamento em água do filme e da fibra revestida, e ensaios de absorção de água em filmes. A degradação dos materiais foi monitorada a partir de testes mecânicos. Os dados obtidos de filmes foram tratados segundo modelagem de Arrhenius para previsão do tempo de vida útil do polímero... Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: Accelerated aging conditions were used to evaluate polymer degradation process in laboratory. The material in study is used isolated of the U.V. radiation component of sunlight. Aging was simulated under diferents temperatures, isothermally. The resin named LMPI 3/2 was developed on a previous work between UNICAMP and CPqD / Telebrás. The U.V. curable acrylic resin consisted of epoxy acrylate and urethane acrylate oligomers, reactive monomer, photoinitiator and inhibitor. Simultaneously, were investigated two commercials resins named CN and CI. Considering that the resins were used as optical fibers coating, the same aging conditions were used with coated fibers. An important characteristic of glass fibers and other glass structures is their tendency to weaken under the combined influence of water vapour and applied load. The effect of the moisture on strength of coated optical fibers and films was also evaluated. The degradation was evaluated by mechanical testing. An Arrhenius model was used to utilize the mechanical properties of the films, providing service life estimation. Mechanical properties of the films versus aging time values were plotted to establish the effect of the enviromment on the strength of the coated optical fibers. The methodology developed in this work provides a fast way to predict the service life of the polymeric coating materials... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Mestre em Engenharia Química
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/267300 |
| Date | 19 April 1991 |
| Creators | Lopes, Elizabeth Borges |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Bittencourt, Edison, 1941-, Agnelli, Jose Augusto M., Mei, Lúcia Helena Innocentini |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 100f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0125 seconds