Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016. / Made available in DSpace on 2017-05-31T14:12:17Z (GMT). No. of bitstreams: 1
345567.pdf: 8768611 bytes, checksum: 8091bbf8621db6062d55cdf9eea64ac2 (MD5)
Previous issue date: 2016 / Compósitos do sistema LZS+Al2O3 foram obtidos por meio de duas rotas de processamento. Na Rota A, o sistema LZS (19,58Li2O.11,10ZrO2. 69,32SiO2) foi obtido a partir da fusão das matérias-primas (carbonato de lítio, quartzo e silicato de zircônio). As fritas obtidas foram moídas e misturadas com nanopartículas de Al2O3 (13 nm; 1-5 %). Na Rota B, os sistemas LZS e LZS+Al2O3 foram obtidos por meio do processamento coloidal de óxidos nanoestruturados de precursores (SiO2, ZrO2, Al2O3 e um precursor de lítio obtido da reação de Li2CO3 e ácido acético). As suspensões obtidas foram congeladas em nitrogênio líquido e liofilizadas. As nanoestruturas obtidas apresentaram ~25 nm de diâmetro. Os pós resultantes das duas rotas foram conformados por prensagem uniaxial e colagem de fitas. Posteriormente foram sinterizados e suas propriedades foram avaliadas. A incorporação de nanopartículas de Al2O3 em matriz LZS reduziu significativamente o coeficiente de expansão térmica (CET). Os compósitos obtidos por meio da Rota A sinterizados a 900 ºC obtiveram densidades relativas de 92 a 98%, apresentaram silicato de zircônio e espodumênio-ß como principais fases cristalinas, dureza entre 4,6 e 6 GPa, módulo de elasticidade entre 78 e 111 GPa. Por outro lado, os compósitos nanoestruturados, produzidos pela Rota B apresentaram as fases cristalinas Li2ZrSi6O15, dissilicato de lítio, e silicato de zircônio. A baixa sinterabilidade dos compósitos, demonstrou a necessidade do uso de técnicas não convencionais de sinterização, como o Spark Plasma Sintering (SPS). Os curtos tempos de processo de SPS (1 min), não permitem que a zircônia reaja para formar silicato de zircônio, já que a evolução das fases depende da reação da alumina para formar outras fases cristalinas. O CET obtido pelos compósitos sinterizados por SPS não resultou tão baixo quanto aos sinterizados de forma convencional, no entanto, tiveram as maiores densidades e melhores propriedades mecânicas, ou seja, dureza entre 5 e 9 GPa e módulo de elasticidade entre 78 e 105 GPa. Após processamento coloidal dos pós obtidos pelas duas rotas de processamento, foram produzidas fitas flexíveis, homogêneas, livre de trincas e de fácil descolagem do substrato. Arquiteturas complexas foram obtidas, como laminados 4 camadas com concentrações graduais de nanopartículas de Al2O3, o vitrocerâmico LZS foi laminado em bicamadas com o aço inoxidável AISI 316L e o compósito nanoestruturado 5AnB com wafer de silício e foram obtidas bicamadas livres de trincas e delaminações.<br> / Abstract : LZS/Al2O3 composites were obtained by two processing routes. In Route A, the LZS system (19.58Li2O·11.10ZrO2·69.32SiO2) was obtained by melt of raw materials (lithium carbonate, quartz and zirconium silicate). The frits were milled and mixed with Al2O3 nanoparticles (13 nm; 1-5vol.%). In Route B, the LZS and LZS + Al2O3 systems were obtained by colloidal processing of the oxide precursors nanoparticle (SiO2, ZrO2, Al2O3, and a lithium precursor obtained by reaction of Li2CO3 and acetic acid). The suspensions were frozen in liquid nitrogen and lyophilized. The nanostructure obtained showed ~ 25 nm in diameter. The resulting powders of the two routes were conformed by uniaxial pressing and tape casting. Subsequently, they were sintered and their properties were evaluated. The Al2O3 addition resulted in reduced the coefficient of thermal expansion (CTE). The composites obtained through Route A sintered at 900 ºC obtained relative densities of 92 to 98%, presented zirconium silicate and ß-spodumene as the main crystalline phases, hardness between 4.6 and 6 GPa, modulus of elasticity between 78 and 111 GPa. On the other hand, the nanostructured composites produced by Route B presented the crystalline phases Li2ZrSi6O15, lithium disilicate, and zirconium silicate. The low sinterability of the composites demonstrated the need for the use of non conventional sintering techniques, such as Spark Plasma Sintering (SPS). The short SPS process times (1 min) do not allow the zirconia to react to form zirconium silicate, since the evolution of the phases depends on the reaction of the alumina to form other crystalline phases. The CTE obtained by the composites sintered by SPS was not as low as conventional sintered, however, they had the highest densities and better mechanical properties, that is, hardness between 5 and 9 GPa and modulus of elasticity between 78 and 105 GPa. After colloidal processing of the powders obtained by the two processing routes, flexible, homogeneous strips were produced, free of cracks and easy take-off of the substrate. Complex architectures were obtained as 4 layer laminates with graded concentrations of Al2O3 nanoparticles, the LZS glass ceramic was laminated in bilayers with AISI 316L stainless steel and 5AnB nanostructured composite with silicon wafer and freezings were obtained from cracks and delaminations.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/176055 |
| Date | January 2016 |
| Creators | Arcaro, Sabrina |
| Contributors | Universidade Federal de Santa Catarina, Oliveira, Antonio Pedro Novaes de, Botella, Rodrigo Moreno |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 208 p.| il., gráfs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |