The newfound capability of creating moisture sensitive interference multilayered thin films (MLTFs) comprising microfibrillated cellulose and polymers has not previously been possible to implement on surfaces other than silicon wafer strips. Being able to incorporate interference MLTFs on fibre-based materials would introduce the possibility for new applications within authentication, sensing and customer attraction for the paper and packaging industry. By using trichloro (1H, 1H, 2H, 2H-perfluorooctyl) silane we were able to hydrophobically modify silicon substrates, enabling interference MLTF lift-off and thus the creation of free-standing MLTFs of approximately 400 nm thickness. Contact dried MLTFs approximately 250 nm thick, were successfully transferred to copy- and filter paper as well as to cellulose-based dialysis membranes. We can also report on the successful synthesis of interference MLTFs directly on a fibre composite material and on aluminium. Initial tests of a method to quantify the pull-off conditions of the MLTFs from the fluorinated surfaces using the Micro Adhesion Measurement Apparatus showed promising results.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-11398 |
Date | January 2008 |
Creators | Holmqvist, Johan |
Publisher | Linköpings universitet, Institutionen för fysik, kemi och biologi, Institutionen för fysik, kemi och biologi |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0013 seconds