Previous issue date: 2015-08-27 / CAPEs / No presente trabalho foram produzidos compósitos a base de epóxi reforçados com liga quasicristalina AlCuFe, para ensaios de microabrasão e molhabilidade. A liga AlCuFe foi produzida num forno de indução de soleira fria com materias de até 99,99% de pureza e submetida ao tratamento térmico por 24h a uma temperatura de 750°C. O quasicristal foi utilizado na forma de pó após moagem em moinho planetário. A caracterização do quasicristal (QC) foi realizada com uso das técnicas de difração de raios x (DRX) e microscopia eletrônica de varredura (MEV). Análises de DRX mostraram fase cristalina bem definida para amostras de QC, por sua vez imagens de MEV indicaram morfologia arredondada do QC e com uso do software IMAGE J, foi possível observar diâmetros de partícula em torno de 5,48±1,83μm. Em adição, o pó metálico foi misturado com uma resina epóxi em proporções de 5%, 10% e 15% em volume, sendo a cura estabelecida em temperatura ambiente. Por sua vez, as propriedades de molhabilidade e microabrasão foram avaliadas. Verificamos que, com o aumento na proporção em volume de quasicristal no compósito, ocorreram alterações significativas no módulo do coeficiente de desgaste, bem como obtenção de maiores valores no ângulo de contato, tornando o material mais hidrofóbico. As imagens de MEV do compósito indicaram os mecanismos de desgaste envolvidos durante o ensaio de microabrasão, levando ao aumento da taxa de desgaste em função da proporção volumétrica de QC no compósito. / In this paper were produced epoxy-based composites reinforced with quasicristalina league AlCuFe to microabrasion and wettability tests. The AlCuFe alloy was produced in a cold hearth induction furnace with materials of up to 99.99% purity and subjected to heat treatment for 24 hours at a temperature of 750 ° C. The quasicristal was used in powder form after milling in a planetary mill. The characterization of quasicristal (QC) has been performed using the techniques of X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD analysis showed well defined crystalline phase for QC samples in turn SEM images indicated rounded morphology and QC using Image J software, it was possible to observe particle diameters around 5.48 ± 1,83μm. In addition, the metal powder was mixed with an epoxy resin proportions of 5%, 10% and 15% by volume being established cure at room temperature. In turn, the properties of wettability and microabrasion were evaluated. We found that, with increasing volume ratio of the composite quasicristal, significant changes in the wear coefficient module and obtaining the higher values of contact angle, making it more hydrophobic. The composite SEM images indicate the wear mechanisms involved during microabrasion test, leading to increased wear rate as a function of the volumetric ratio of QC in the composite.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/17704 |
| Date | 27 August 2015 |
| Creators | MARTINS, José Lucas Pessoa |
| Contributors | http://lattes.cnpq.br/5515185093886020, ALVES, Kleber Goncalves Bezerra, CAVALCANTE, Danielle Guedes de Lima |
| Publisher | Universidade Federal de Pernambuco, Programa de Pos Graduacao em Engenharia Mecanica, UFPE, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Breton |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE |
| Rights | Attribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds