Orientador: Celia Marisa Rizzatti-Barbosa / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-22T22:45:14Z (GMT). No. of bitstreams: 1
Pitta_MariaSuzanaSchmidt_M.pdf: 3666397 bytes, checksum: 33e4befacc233ce608c609e61a4a6fc8 (MD5)
Previous issue date: 1997 / Resumo: Em Prótese Dental, as técnicas para polimerizar resinas acrílicas tem sido melhoradas com o objetivo de minimizar as distorções que ocorrem durante as diversas fases do processamento. e que podem causar alterações nas próteses totais e/ou removíveis, com conseqüentes traumas oc1usais e injúrias aos tecidos subjacentes. Este estudo tem por objetivo mensurar a variação na inclinação das cúspides mésio palatinas dos primeiros molares superiores de próteses totais após processamento, por três métodos diferentes. Para isto, foram confeccionadas, a partir de um modelo metálico representando uma maxila edêntula, 30 próteses totais superiores com as mesmas características quanto à espessura, forma e montagem dos dentes. As próteses foram divididas em três grupos de 10 amostras e foram polimerizadas por diferentes técnicas. As próteses do Grupo I foram polimerizadas por banho de água aquecida a 73°e durante, 9 horas, as próteses do Grupo II foram polimerizadas por energia de microondas a 440 W durante 4 minutos, e as próteses do Grupo III foram polimerizadas por energia de microondas a 80 W durante 15 minutos. Os ângulos formados pela intersecção das retas que representavam o prolongamento das vertentes triturantes das cúspides mésio palatinas dos primeiros molares superiores foram medidos antes da polimerização, após a
polimerização e após o polimento. Os dados foram submetidos a análise estatística descritiva por não apresentarem distribuição normal. Foram confeccionadas matrizes de correlação para os ângulos medidos e encontrou-se que entre a passagem da fase de pré polimerização para a fase de pós-polimerização houve uma melhor aproximação dos ângulos (34%) para o Grupo II e que houve diferenças significativas entre as fases de pós polimerização e polimento, com grande discrepância para os três grupos, sendo 57% de aproximação para o Grupo I, 37% para o Grupo II e apenas 7% para o Grupo III, mesmo tendo sido utilizado o mesmo método de polimento para os três grupos. A partir destes dados iniciais, foram calculados a média, variância e desvio padrão. das variações angulares ocorridas na passagem das fases de pré polimerização para pós polimerização e na passagem das fases de pós polimerização para polimento. Os dados da matriz de correlação da Variância das variações angulares foram, para o Grupo I = 19% de aproximação, para o Grupo II = 54% e para o Grupo III = 33%. Os resultados das matrizes de correlação do Desvio Padrão entre as variações angulares foram: para o Grupo I = 24% de aproximação, para o Grupo II = 62% e para o Grupo III = 30%.
Considera-se que a técnica mais eficiente deva apresentar coeficiente de correlação mais próximo da unidade, significando que os ângulos sofreram poucas alterações durante os procedimentos. Dessa forma, pudemos constatar que: 1. Os três métodos estudados apresentaram alterações nas inclinações das cúspides. 2. O método de polimerização por energia de microondas a 440W por 4 minutos foi o que apresentou menor alteração nas inclinações das cúspides dos dentes estudados. 3. O polimento pelo método convencional alterou significativamente a inclinação das cúspides das amostras estudadas / Abstract: In Dental Prosthesis, the techiques to polymerize acrylic resins have been improved with the objective to minimize the distortions that occur during the several phases of execution and that may cause alteration in total and/or partial removable prosthesis, with subsequent occlusal trauma and injury to underlying tissues. The purpose of this is to measure the variation in the mesial palatine cuspids inclination in the first superior molars of total prosthesis, after polymerization by three different methods. To achieve this goal, it has been prepared 30 complete dentures with the same characteristcs, after what they were divided into three groups. The dentures of the Group I were polymerized with hot water bath tecnique at 73° C during 9 hours; the dentures of the Group II were polymerized with microwave energy at 440 W during 4 minutes, the dentures of the Group III were polimerized with microwave energy at 80 W during 15 minutes. The angles obtained by the intersection of the two straight lines representing the extension of the crushing slopes of the mesial palatine cuspids of the first superior molars were measured before and after polymerization and after polishing. The data was submitted to analysis using descriptive statistics, as it did not presented a normal distribution. It has been prepared correlation matrices for all the mesured angles and it has been found that during the phase pre-polymerization to post-polymerization the angles of the Group II had a better approach (34%). During the phase post-polymerization to polishing have occurred significant differences, with great discrepancy among the three groups (57% of approach for the Group I, 37% of approach for the Group II and 7% of approach for the Group III), even considering that it has been used the same polishing method for all the groups. Starting with this initial data, it has been calculated the mean, variance and standard deviation of the angular variations occurred during the phase pre-polymerization to post-polymerization and during the phase post-polymerization to polishing. The results of the variance correlation matrix of the angular variations were, for Group I, 19% of approach, for Group II, 54% and for Group III, 33%. The results of the standard deviation correlation matrix of the angular variations wee for Group I, 24% of approach, for Group II, 62% and for Grupo III, 30%. The most efficient technique shall result in correlation coefficient near 1, what means that the angles had small alterations during the process. ... Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Fisiologia e Biofisica do Sistema Estomatognatico / Mestre em Odontologia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290526 |
| Date | 10 October 1997 |
| Creators | Pitta, Maria Suzana Schmidt |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Rizzatti-Barbosa, Celia Marisa, 1957-, Bottino, Marco Antonio, Guimarães, Alcides |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 125f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds