Previous issue date: 2014-12-19 / Existe uma grande dificuldade na forma??o de um comp?sito do metal refrat?rio
de ni?bio com o cobre. Isto se deve ao fato de que o sistema Nb-Cu ? quase mutuamente
imisc?vel, podendo ser desprezada a solubilidade entre eles. Estas propriedades
dificultam ou impedem a obten??o de estruturas homog?neas e de alta densidade,
convencionalmente preparadas. Este trabalho tem por objetivo analisar a utiliza??o do
processo de moagem de alta energia (MAE) para transpor estas dificuldades naturais,
no que se refere ? densifica??o dos corpos sinterizados. A MAE e a prensagem foram
utilizadas na prepara??o dos p?s, para a obten??o de uma fina e homog?nea distribui??o
do tamanho dos gr?os. Quatro cargas de p?s de Nb e Cu contendo 15% em massa de Cu
foram ent?o mo?dos por MAE em um moinho de bolas tipo planet?rio, sob diferentes
per?odos e velocidades de moagem. Os resultados obtidos pela MAE foram analisados
atrav?s da microscopia eletr?nica de varredura (MEV), de acordo com os par?metros de
tempo e velocidade de moagem. As amostras foram compactadas sob press?o de 200
MPa, em seguida foram sinterizadas por fase l?quida em um forno ? v?cuo nas
temperaturas de 1100?C/60 min e 1200?C/60 min. Depois foi utilizada a t?cnica de
caracteriza??o de difra??o de raios-X para a identifica??o das fases. As microestruturas
das amostras sinterizadas foram observadas e avaliadas atrav?s de microscopia
eletr?nica de varredura (MEV). Ensaios de Microdureza Vickers foram realizados,
obtendo maiores valores para os corpos sinterizados nos maiores tempos de moagem
dos p?s e para as maiores velocidades de moagem. Foi verificado que a sinteriza??o por
fase l?quida das amostras que foram processadas por MAE, produziu no final uma
estrutura homog?nea e densificada em 77,4% em rela??o ao valor da densidade te?rica
do comp?sito / There is great difficulty in forming a composite refractory metal niobium with
copper. This is due to the fact that Nb-Cu system is almost mutually immiscible and may
be neglected solubility between them. These properties hinder or prevent obtaining
homogeneous and high-density structures, conventionally prepared. This study aims to
analyze the use of high-energy milling process (MAE) to implement these natural
difficulties, with regard to the densification of the sintered bodies. The MAE and the press
were used in the preparation of powders, to obtain a fine and homogeneous distribution
of the grain size. Four loads Nb and Cu powders containing 15% by weight of Cu were
then milled for MAE in a planetary type ball mill under various milling times and speeds.
The results obtained by MAE were analyzed by scanning electron microscopy (SEM),
according to the parameters of time and grinding speed. The samples were compacted
under pressure of 200 MPa, were then sintered in liquid phase in a vacuum furnace at
temperatures of 1100 ? C / 60 min and 1200 ? C / 60 min. Then it was used to characterize
diffraction of X-rays to identify the phases. The microstructures of the sintered samples
were observed and evaluated using scanning electron microscopy (SEM). Vickers
Microhardness tests were performed, obtaining higher values for the sintered bodies in
the largest of the post milling times and the larger grinding speeds. It was found that the
liquid phase sintering of the samples that were processed by MAE produced at the end of
a homogeneous and densified structure in 77,4% relative to the value of the theoretical
density of the composite
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/19594 |
| Date | 19 December 2014 |
| Creators | Lima, H?rik Dantas de |
| Contributors | 05012180410, http://lattes.cnpq.br/9858094266525225, Silva, Ariadne de Souza, 00735940401, http://lattes.cnpq.br/5623381698478389, Costa, Francin? Alves da, 45327220478, http://lattes.cnpq.br/8698567925323942, Filgueira, Marcello, 77881931434, http://lattes.cnpq.br/0725750287341168, Gomes, U?lame Umbelino |
| Publisher | Universidade Federal do Rio Grande do Norte, PROGRAMA DE P?S-GRADUA??O EM CI?NCIA E ENGENHARIA DE MATERIAIS, UFRN, Brasil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds