AlÃvio de tensÃes residuais em junta soldada com arame de baixa temperatura de transformaÃÃo martensÃtica / Residual stress relief in welded joint with martensitic low transformation temperature wire

FundaÃÃo Cearense de Apoio ao Desenvolvimento Cientifico e TecnolÃgico / CoordenaÃÃo de AperfeÃoamento de Pessoal de NÃvel Superior / A soldagem multipasse de chapas grossas impÃe à junta soldada um estado de tensÃes residuais que pode ser muito prejudicial quando estas estÃo em serviÃo. Existem vÃrios fenÃmenos capazes de alterar os nÃveis de tensÃes residuais de soldagem nos materiais, um deles à a transformaÃÃo de fases. Este trabalho apresenta um estudo comparativo dos nÃveis de tensÃes residuais em trÃs juntas soldadas, produzidas com metais de adiÃÃo diferentes pelo processo arame tubular. Um arame eletrodo de aÃo inoxidÃvel martensÃtico Fe-12%Cr-5%Ni com baixa temperatura de transformaÃÃo foi o primeiro a ser utilizado, o segundo, um aÃo inoxidÃvel austenÃtico Fe-18,5%Cr-10%Ni, e finalmente, um aÃo baixa liga Fe-1,25%Cr-0,5%Mo. No processo de soldagem foi utilizada uma bancada robotizada com fonte multiprocesso para confecÃÃo das juntas, sendo o aÃo ABNT 4140 o metal de base. As tensÃes residuais foram medidas na superfÃcie das juntas soldadas atravÃs do mÃtodo de difraÃÃo de raios-X. TambÃm foram avaliadas as seguintes propriedades mecÃnicas; resistÃncia à traÃÃo, tenacidade e microdureza, bem como, as microestruturas resultantes na zona fundida, zona afetada pelo calor e metal de base. Os resultados mostraram que a junta produzida com arame eletrodo que sofreu transformaÃÃo martensÃtica a baixa temperatura apresentou nÃveis considerÃveis de tensÃo residual compressiva, ao contrÃrio das demais juntas que apresentaram tensÃo residual trativa na maioria dos pontos medidos. Nos ensaios de traÃÃo, a junta de baixa temperatura de transformaÃÃo martensÃtica apresentou elevados limites de escoamento e de resistÃncia à traÃÃo, e a sua ruptura ocorreu na interface entre o metal de base e o metal de solda. Nos ensaios de impacto da mesma junta, os valores de energia absorvida no metal de solda e zona termicamente afetada se apresentaram relativamente baixos. / The multi-pass welding of thick plates imposes to the welded joint a state of residual stresses that can be very harmful when they are in service. There are various phenomena that can alter the levels of residual stresses after materials welding; one of them is phase transformation. This work presents a comparative study of the levels of residual stresses in three welded joints, produced with different filler metals by Flux Cored Arc Welding (FCAW). A martensitic stainless steel wire Fe-12% Cr-5% Ni with low transformation temperature was the first to be used. After this an austenitic stainless steel Fe-18.5% Cr-10% Ni was used and finally a low alloy steel Fe -1.25% Cr-0.5% Mo. In the welding process, we used a workbench robot with multiprocess source for making joints, and the AISI 4140 the base metal.. Residual stresses were measured on the surface of welded joints using X-ray diffraction method. Tensile strength, toughness and hardness, as well as the resultant microstructure in weld metal, heat affected zone and base metal were evaluated. The results showed that the joint produced with wire electrode that has undergone low temperature martensitic transformation presents significant levels of compressive residual stress, unlike the other joints which present tensile residual stress at most of the measured points. In tensile tests, the joint of martensitic stainless steel showed high yield limits and tensile strength, and its rupture occurred at the interface between base metal and weld metal. Results of the impact tests of this joint showed relatively low absorbed energy values at the weld metal and heat affected zone.

Identiferoai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:10115
Date25 September 2015
CreatorsFrancisco Josà dos Santos Oliveira
ContributorsHamilton Ferreira Gomes de Abreu, Cleiton Carvalho Silva, Rodrigo Freitas GuimarÃes
PublisherUniversidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Formatapplication/pdf
Sourcereponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds