Matériaux innovants pour la rétention sélective de césium et de strontium à partir de solutions aqueuses multi-composants : synthèse, optimisation et évaluation des performances / Innovative materials for selective retention of cesium and strontium from aqueous multi-component solutions : synthesis, optimization and assessment of performance

Ce travail porte sur la synthèse et la caractérisation de nouveaux matériaux afin de proposer une alternative dans le cadre de la dépollution nucléaire. Dans une première partie bibliographique, les principaux matériaux inorganiques utilisés pour ce procédé sont décrits en précisant leurs capacités de sorption. Les matériaux lamellaires apparaissent comme possédant un fort potentiel pour cette application. Deux solides ont retenu notre attention : les nanostructures à base de vanadates et de manganates.Des synthèses solvothermales sous flux micro-ondes de ces composés sont ensuite développées, afin d’obtenir une structuration sous forme de nanotubes de vanadates et de nanofleurs de manganates. Une optimisation des vanadates a ainsi été menée en évaluant l’impact de différents facteurs (par exemple, temps de maturation, temps de chauffage, nature et quantité de templates) sur les propriétés structurales et texturales des produits synthétisés. L’enroulement des feuillets est fortement influencé à la fois par la quantité d’amine et sa structure chimique. En effet, seules les amines à longue chaîne conduisent à l’obtention de nanotubes de façon homogène. Une analyse structurale a également été menée pour les deux types de composés en couplant les données expérimentales et celles obtenues par simulation.Les performances de sorption et la sélectivité des matériaux dans différents milieux (eau ultra-pure, eau de rivière) ont été évaluées vis-à-vis du césium et du strontium, seuls ou en mélange. Les résultats montrent clairement une sélectivité très forte des vanadates vis-à-vis du Cs+ et des manganates pour le Sr2+, même en milieu compétitif.La calorimétrie et la simulation moléculaire ont finalement été couplées pour mieux décrire les processus de sélectivité. / This work focuses on the synthesis and characterization of new nanostructured materials that can be potentially proposed as alternatives in the field of nuclear decontamination. The first part is devoted to the state of the art on the use of inorganic materials for decontamination purposes, with the emphasis placed on their sorption capacity and selectivity. The layer materials are considered as offering potential for such applications. In consequence, the main efforts in this work have been focused on manganate and vanadate nanostructures.Solvothermal synthesis of these materials was developed on the basis of micro-wave oven procedures to control the materials structuring, thus leading to vanadate nanotubes and manganate nanoflowers. The optimization of vanadates was carried out by taking into account the effect of various factors (e.g., duration of maturation and heating stages, nature and mass of the template) on both the structural and textural properties of the resulting substrates. It was demonstrated that the scrolling of the layers was strongly influenced by the amount of amine and its chemical structure. Indeed, only the amine templates possessing long chains allowed homogeneous nanotubes to be achieved. More information about the structuring process was inferred when coupling experimental and simulation approaches.The sorption performance of the resulting solid materials in terms of sorption capacity and selectivity was assessed in model and simulated systems obtained by using either ultrapure or river water with an adequate composition as solvent to prepare aqueous solutions of strontium or/and cesium. The results of sorption experiments clearly indicated strong selectivity of the vanadate structures toward Cs+ and that of the manganate ones toward Sr2+, even under conditions of competition among various ionic species.Direct calorimetry measurements of heat effects accompanying sorption were correlated with the results of molecular simulation studies to shed more light on the origin of the improved sorption selectivity.

Identiferoai:union.ndltd.org:theses.fr/2017MONTT168
Date06 October 2017
CreatorsAlby, Delhia
ContributorsMontpellier, Zajac, Jerzy
Source SetsDépôt national des thèses électroniques françaises
LanguageFrench
Detected LanguageFrench
TypeElectronic Thesis or Dissertation, Text

Page generated in 0.002 seconds