Nanofibrillated cellulose (NFC) from wood is an interesting material constituent of high strength and high aspect ratio, which easily forms networks through interfibril secondary bonding including hydrogen bonds. This has been exploited in preparation of new materials, which extend the range of properties for existing cellulosic materials. The objective is to explore processing-structure and structure-property relationships in NFC materials. Dense networks of NFC, referred to as “nanopaper” having a random-in-the-plane orientation of the fibrils have been successfully prepared by a papermaking-like process involving vacuum filtration and water evaporation using laboratory papermaking equipment. Large, flat and transparent nanopaper sheets have thus been prepared in a relatively short time. Using the same preparation route, NFC was used to reinforce pulped wood fibers in dense network structures. NFC networks formed in the pore space of the wood fiber network give an interesting hierarchical structure of reduced porosity. These NFC/wood fiber biocomposites have greater strength, greater stiffness and greater strain-to-failure than reference networks of wood fibers only. In particular, the work to fracture (area under the stress-strain curve) is doubled with an NFC content of only 2%. The papermaking preparation route was extended to prepare nanocomposites of high NFC content with a cellulose derivative matrix (hydroxyethyl cellulose, HEC) strongly associated to the NFC. Little HEC was lost during filtration. The NFC/HEC composites have high work to fracture, higher than that of any reported cellulose composite. This is related to NFC network characteristics, and HEC properties and its nanoscale distribution and association with NFC. Higher porosity NFC nanopaper networks of high specific surface area were prepared by new routes including supercritical drying, tert-butanol freeze-drying and CO2 evaporation. Light-weight porous nanopaper materials resulted with mechanical properties similar to thermoplastics but with a much lower density and a specific surface area of up to 480 m2/g. Freeze-drying of hydrocolloidal NFC dispersions was used to prepare ultra-high porosity foam structures. The NFC foams have a cellular foam structure of mixed open/closed cells and “nanopaper” cell wall. Control of density and mechanical properties was possible by variation of NFC concentration in the dispersion. A cellulose I foam of the highest porosity ever reported (99.5%) was prepared. The NFC foams have high ductility and toughness and may be of interest for applications involving mechanical energy absorption. Freeze-drying of NFC suspended in tert-butanol gave highly porous NFC network aerogels with a large surface area. The mechanical behavior was significantly different from NFC foams of similar density due to differences in deformation mechanisms for NFC nanofiber networks. / QC 20110406
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-32079 |
| Date | January 2011 |
| Creators | Sehaqui, Houssine |
| Publisher | KTH, Fiber- och polymerteknik, Stockholm : KTH Royal Institute of Technology |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Trita-CHE-Report, 1654-1081 ; 2011:024 |