Orientadores: Peter Jurgen Tatsch, Stanislav A. Moshkalyov / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Eletrica e de Computação / Made available in DSpace on 2018-08-05T15:04:36Z (GMT). No. of bitstreams: 1
Nunes_AlcineiMoura_M.pdf: 4164375 bytes, checksum: 7cc7a3a84a2aa99efc455551e270bc57 (MD5)
Previous issue date: 2005 / Resumo: Este trabalho apresenta os resultados e as discussões dos mecanismos de corrosão por plasma de filmes de silício policristalino e nitreto de silício para aplicações em dispositivos MEMS e CMOS. A corrosão foi feita em um reator convencional de corrosão por plasma em modo RIE (Reactive Ion Etching). Para aplicação em MEMS, corrosões de silício policristalino com perfis anisotrópicos e seletividade maior que 10 para óxido de silício foram obtidos. As misturas gasosas utilizadas na corrosão foram: SF6/CF4/CHF3 e SF6/CF4/N2. Processos híbridos, utilizando duas etapas de corrosão em condições diferentes, num mesmo processo, foram feitos para possibilitar a obtenção de perfis altamente anisotrópicos, com seletividade elevada. Para avaliar melhor a evolução do perfil de corrosão, foram utilizadas amostras com filmes espessos de silício policristalino (>3mm). Para aplicação em eletrodo de transistores CMOS, afinamento de linhas de 5mm para 1mm de largura foram obtidos com perfil anisotrópico (A~0,95) em processos híbridos, utilizando uma primeira etapa de corrosão com condições de maior bombardeio iônico e menor seletividade, e uma segunda etapa com menor bombardeio iônico e maiores seletividades para o óxido e fotorresiste. Corrosões de nitreto de silício (SiNx), com seletividade elevada são imprescindíveis para aplicação em tecnologia LOCOS. Resultados de corrosões e filmes de nitreto de silício para esta aplicação foram feitas utilizando as seguintes misturas gasosas: CF4/O2/N2, CF4/H2, SF6/CF4/N2 e CHF3/O2. As Maiores seletividades obtidas foram de aproximadamente 10 para óxido e aproximadamente 7 para o substrato de silício. Os filmes foram caracterizados com vários equipamentos. Um Perfilômetro foi utilizado para medir a profundidade das corrosões, e por conseguinte, calcular a taxa de corrosão através da divisão pelo tempo. Um Elipsômetro foi utilizado para medir as espessuras e índices de refração dos filmes utilizados. O FTIR (Fourier Transform Infrared Spectrocopy) foi utilizado para caracterizar a composição do filme de nitreto de silício após o tratamento térmico. Imagens SEM (Scanning Electron Microscopy) dos filmes corroídos foram feitas para analisar o perfil e mecanismo de corrosão para cada mistura / Abstract: This work presents the results and the discussion about mechanisms of plasma etching of polysilicon and silicon nitride films for applications in MEMS and CMOS devices. The etching was performed in a conventional reactor of plasma etching in a RIE mode (Reactive Ion Etching). For application in MEMS, polysilicon etching with anisotropic profile and high selectivity (>10) for silicon oxide was obtained. The mixtures used in etching were SF6/CF4/CHF3 and SF6/CF4/N2. Hybrid processes, using two etching stages in different conditions, in the same etching process, were done as possible solutions for highly anisotropic profiles with elevated selectivity. The evolution of the etching profile is better evaluated using polysilicon thick films (>3mm). For application in CMOS transistors electrode, 5mm to 1mm thinning was obtained with anisotropic profile (A~0,95) in hybrids processes, using the first stage in conditions with elevated ionic bombardment and reduction selectivity, and the second stage with reduction ionic bombardment and elevated selectivity to the oxide and photorresist. Highly selective silicon nitride etching (SiNx) is necessary for application in LOCOS technology. Results of the etching and silicon nitride films for this application was performed using the following mixtures: CF4/O2/N2, CF4/H2, SF6/CF4/N2 and CHF3/O2. High selectivity was obtained for silicon oxide (>10) and silicon substrate (~7). The films were characterized by various equipment. The Profiler was used to measure the etching depth, and herewith, the etching rate was evaluated. The Elipsometer was used to measure the refractive index and width of the films. FTIR (Fourier Transform Infrared Spectroscopy) was used to characterize the composition of the nitride film after the thermal treatment. SEM (Scanning Electron Microscopy) images of the etched films were done to analyse the profile and the etching mechanism for each mixture / Mestrado / Microeletronica / Mestre em Engenharia Elétrica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/261834 |
Date | 13 May 2005 |
Creators | Nunes, Alcinei Moura |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moshkalev, Stanislav, 1952-, Tatsch, Peter Jürgen, 1949-, Diniz, José Alexandre, Doi, Ioshiaki, Damiani, Furio, Monteiro, Marcelo de Jesus R. |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Elétrica e de Computação |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 151p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |