Flip Chip in Package (FCIP) has been developed to achieve the assembly process with area array interconnects. Particularly, a high I/O count coupled with finer pitch area array interconnects structured FCIP can be achieved using no-flow underfill assembly process. Using the assembly process, a high, stable yield assembly process recently reported with eutectic lead-tin solder interconnections, 150 µm pitch, and I/O counts in excess of 3000. The assembly process reported created a large number of voids among solder interconnects in FCIP.
The voids formed among solder interconnections can propagate, grow, and produce defects such as solder joint cracking and solder bridging. Moreover, these voids can severely reduce reliability performance. Indeed, many studies were conducted to examine the void formation in FCIP. Based on the studies, flip chip geometric design, process conditions, and material formulation have been considered as the potential causes of void formation. However, the present research won't be able to identify the mechanism of void formation, causing a lot of voids in assembly process without consideration of chemical reaction in the assembly process with a fine-pitch, high I/O density FCIP.
Therefore, this research will present process technology necessary to achieve high yields in FCIP assemblies using no-flow underfills and investigate the underlying problem of underfill void formation in these assemblies. The plausible causes of void formation will be investigated using experimental techniques. The techniques will identify the primary source of the void formation. Besides, theoretical models will be established to predict the number of voids and to explain the growth behavior of voids in the FCIP. The established theoretical models will be verified by experiments. These models will validate with respect to the relationship between process parameters to achieve a high yield and to minimize voids in FCIP assemblies using no-flow underfill materials regarding process as well as material stand points. Eventually, this research provides design guideline achieving a high, stable yield and void-free assembly process.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/29755 |
| Date | 06 July 2009 |
| Creators | Lee, Sangil |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Detected Language | English |
| Type | Dissertation |
Page generated in 0.002 seconds