Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia, Florianópolis, 2016 / Made available in DSpace on 2016-09-20T04:43:08Z (GMT). No. of bitstreams: 1
340524.pdf: 1227179 bytes, checksum: 595c7fd888031571f3aafdf272327575 (MD5)
Previous issue date: 2016 / O objetivo deste estudo foi avaliar a síntese do pó de tricálcio fosfato em fase beta (ß-TCP) e as propriedades mecânicas de arcabouços (scaffolds) compostos ß-TCP recobertos com polímeros bioabsorvíveis, colágeno e poli L-co-D,L ácido lático (PLDLA). O pó de ß-TCP foi obtido por moagem reativa e, então, caracterizado por difração de raios-X e microscopia eletrônica de varredura (MEV/EDS). Scaffolds de ß-TCP foram obtidos pelo método da replica, no qual esponjas de poliuretano são imersas em uma suspensão de ß-TCP e submetidas a tratamento térmico para remoção do poliuretano e sinterização da cerâmica. Colágeno do tipo I ou PLDLA foram usados para recobrir os arcabouços de ß-TCP pelo método de revestimento por imersão (dip coating). Os scaffolds foram separados em quarto grupos, dependendo do material de recobrimento: sem recobrimento (grupo A), duas imersões em colágeno (grupo B), duas imersões em PLDLA (grupo C) e dez imersões em PLDLA (grupo D). As amostras foram caracterizadas por testes de compressão e MEV/EDS. Análises químicas e microscópicas revelaram morfologia apropriada das partículas de pó e a presença ou ausência de recobrimento polimérico nos arcabouços. Os scaffolds recobertos com PLDLA apresentaram uma maior resistência à compressão (grupo D; 0,11 ? 0,054 MPa / grupo C; 0,025 ? 0,015) do que aqueles com recobrimento por colágeno (grupo B; 0,022 ? 0,012 MPa) ou sem recobrimento (grupo A; 0,024 ? 0,012 MPa). Todas as estruturas porosas formaram uma rede de poros altamente interconectada. A porosidade média dos scaffolds de ß-TCP sem recobrimento foi de 86% e o tamanho de poro foi de 738 µm, em média, enquanto os scaffolds recobertos com 10 camadas de PLDLA tiveram uma porosidade média de 44,6% e de 200 a 400 µm de tamanho de poro. O método de recobrimento com PLDLA revelou-se uma potencial estratégia para aumentar a resistência mecânica de materiais cerâmicos porosos, possibilitando à estrutura desenvolvida uma aplicação clínica como enxerto ósseo inlay. <br> / Abstract : The purpose of this study was to evaluate the synthesis of beta phase tricalcium phosphate (ß-TCP) powder and mechanical properties of scaffolds composed of ß-TCP coated with bioabsorbable polymers, namely collagen and poly D,L-lactic acid (PDLLA). ß-TCP powder was obtained by reactive milling and then characterized by X-ray diffraction and scanning electron microscopy (SEM/EDS). ß-TCP scaffolds were obtained by replica method, in which polyurethane foams are immersed in ß-TCP suspension and thereafter submitted to a thermal treatment to remove the polyurethane and sinter the ceramic. Type-I collagen or PDLLA were used to coat the ß-TCP scaffolds by dip coating method. The scaffolds were separated in four groups depending on the coating material: non-coated (group A), double immersion in collagen (group B), double immersion in PDLLA (group C) and ten immersions in PDLLA (group D). Samples were characterized by compressive tests and SEM/EDS. Chemical and microscopic analyses revealed appropriate morphology of powder particles and scaffolds, with or without polymeric coatings. Scaffolds coated with PDLLA showed higher compressive strength (group D; 0.11 ? 0.054 MPa/ group C; 0.025 ? 0.015) than those of collagen (group B; 0.022 ? 0.012 MPa) or non-coated groups (group A; 0.024 ? 0.012 MPa). All the porous structures formed a highly interconnected pore network. The mean porosity ß-TCP scaffolds free of coatings was around 86% and mean pore size of 738 µm, while scaffolds coated with 10 layers of PDLLA had a mean porosity of about 44.6% and 200 to 400 µm of pore size. The coating method of ß-TCP with PDLLA revealed a potential strategy to increase mechanical strength of porous ceramic materials, given to the developed structure a clinical application as inlay bone graft.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/167998 |
| Date | January 2016 |
| Creators | Magrin, Gabriel Leonardo |
| Contributors | Universidade Federal de Santa Catarina, Benfatti, Cesar Augusto Magalhães, Souza, Júlio César Matias |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 88 p.| il., grafs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |