Orientador: Claudio Airoldi / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-14T17:53:43Z (GMT). No. of bitstreams: 1
Macedo_ThaisRegi_D.pdf: 2848180 bytes, checksum: 54c8b1c12b90c47c6be6008afc371018 (MD5)
Previous issue date: 2009 / Resumo: Este trabalho descreve a preparação, caracterização e aplicação de novos materiais híbridos inorgânico-orgânicos nanoestruturados, obtidos a partir do processo de funcionalização da superfície lamelar de derivados do RUB-18, a forma ácida do material, H-RUB-18, e a forma intercalada com moléculas orgânicas polares, CTA-RUB-18. Para esse processo, foram usados agentes sililantes contendo nitrogênio, enxofre e oxigênio como grupos ativos nas moléculas e dois métodos diferentes. Os difratogramas de raios X mostraram a cristalinidade dos materiais e as microscopias eletrônicas de varredura, a morfologia e o tamanho das partículas formadas. Os espectros de ressonância magnética nuclear de Si e C no estado sólido mostraram que as sínteses foram bem sucedidas. Os resultados obtidos através da análise elementar e da termogravimetria determinaram as quantidades de grupos orgânicos imobilizadas na superfície, o valor máximo obtido foi de 3,79 mmol de grupos por grama de material, um valor próximo da capacidade máxima de funcionalização do material, que é de 3,85 mmol g. Os híbridos nanoestruturados apresentaram estabilidade térmica até aproximadamente 540 K. Os materiais funcionalizados com grupos nitrogenados foram aplicados para a sorção de íons cobre, níquel e cobalto, enquanto os materiais sulfurados foram usados para a sorção de cádmio e chumbo de solução aquosa. As isotermas de sorção foram obtidas pelo processo de batelada, e os dados experimentais foram ajustados aos modelos de Freundlich e Langmuir-Freundlich, considerando superfícies heterogêneas. Esses dados forneceram subsídios para o conhecimento interativo do sistema, considerando a energética da interação. O efeito interativo cátion/centros básicos na interface sólido/líquido foi avaliado através da microcalorimetria e as grandezas termodinâmicas, obtidas nesses sistemas heterogêneos, propiciaram condições para estabelecer ordem energética favorável das interações. Os resultados obtidos mostraram a viabilidade da aplicação dos materiais como eficientes sorventes, para extrair cátions de um ecossistema. / Abstract: The present study describes the preparation, characterization and application of the new inorganic-organic nanostructured hybrid materials, prepared by the functionalization process of the layered surface of derivative RUB-18 material, its acidic, H-RUB-18 and intercalated, CTA-RUB-18 forms. For this process were used silylating agents containing nitrogen, sulfur and oxygen as active atoms on the molecules and two different methods. The X ray diffractograms showed the crystallinity of the materials and the electron scanning microscopy (SEM) the morphology and size of the particles formed. The nuclear magnetic resonance (NMR) spectra for Si and C nuclei in the solid state show that the syntheses were successfully performed. From the obtained elemental analysis and thermogravimetry (TG) results the amount of organic groups immobilized on the surface was determined. The maximum number was 3.79 mmol groups per gram of material, a value near to the maximum of its capacity, 3.85 mmol g. The nanostructured hybrids present thermal stability up to 540 K. The nitrogen functionalized materials were applied for sorption of copper, nickel and cobalt from aqueous solution, while the sulfur materials were used for cadmium and lead sorption from aqueous solution. The sorption isotherms were obtained by the batchwise process and the data were adjusted to the Freundlich and Langmuir- Freundlich models, considering heterogeneous surfaces. These data supply information for the interactive knowledge of the systems, considering the energy of interaction. The interactive effect of cation/basic centers at the solid/liquid interface was evaluated through microcalorimetry and the thermodynamic values, obtained in these heterogeneous systems, give conditions for establishment of a favorable energetic order in the interaction. The obtained results showed the viability of application of the materials as efficient sorbents to extract cations from an ecosystem. / Doutorado / Quimica Inorganica / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/250073 |
| Date | 09 October 2009 |
| Creators | Macedo, Thais Regi |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Airoldi, Claudio, 1942-, Lima, Eder Claudio, Nardo, Regina Celia Galvão Frem di, Mazali, Italo Odone, Formiga, André Luiz Barboza |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 135 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0097 seconds