Previous issue date: 2016-07-27 / Sem bolsa / O advento da adesão na Odontologia permitiu o uso de acessórios ortodônticos cimentados diretamente sobre a superfície dental. Com estes procedimentos adesivos, surge um importante questionamento acerca do método mais indicado para a remoção dos bráquetes e desgaste do agente de cimentação remanescente sobre o esmalte dental. Várias são as técnicas propostas no que tange aos instrumentos de remoção, mas a literatura aponta que, independente da técnica, sempre há dano à estrutura dental. O uso de acessórios ortodônticos, associados ao excesso de agente de cimentação ao redor dos bráquetes, possibilita um maior acúmulo de biofilme e, consequentemente, desenvolvimento de cárie ao redor dos acessórios. Assim, este estudo tem o objetivo adicionar metacrilatos metálicos coloridos - cobre e prata - a cimento ortodôntico experimental e avaliá-los quanto a influência da cor dos novos cimentos na identificação dos excessos, previamente à fotoativação do produto, e no desgaste do remanescente após a descimentação dos acessórios ao final do tratamento. Outro objetivo foi avaliar o efeito antimicrobiano produzido pela adição dos metacrilatos contra o Streptococcus mutans, microorganismo fortemente associado à carie dental. Os grupos testados foram: Cimento ortodôntico experimental sem metacrilato metálico (C), Cimento ortodôntico experimental com Metacrilato de Prata (CMAg), Cimento ortodôntico experimental com Metacrilato de Cobre (CMCu) e referências comerciais - cimento ortodôntico convencional (Transbond XT, 3M Unitek, Monrovia, CA, EUA) e resina composta de coloração distinta da estrutura dental (Resina Composta Filtek Z250 XT D3, 3M ESPE, St Paul, MN, USA). Os materiais foram caracterizados quanto ao grau de conversão, propriedades colorimétricas, propriedades físicas, químicas e mecânicas, viabilidade celular e efeito antibacteriano (através de Teste de Difusão e Ágar e Teste de Contato Direto Modificado). O tempo utilizado na cimentação e remoção dos bráquetes foi avaliado e a superfície do esmalte foi caracterizada em microscopia eletrônica de varredura (MEV), bem como a perda estrutural de esmalte, resultante da remoção do agente de cimentação residual, foi avaliada através da Perfilometria 3D (Rugosidade superficial - Sa e volume de esmalte perdido - V). Os procedimentos experimentais de cimentação, remoção e desgaste do remanescente de cimento foram realizados por operador experiente. Para todos os testes foi considerado o valor p<0,05 como estatisticamente significante. Através dos testes realizados, foi possível identificar que os CMCu e CMAg podem ser potencialmente antimicrobianos, uma vez que apresentaram halo de inibição maior que os dos demais grupos. CMCu inibiu o crescimento microbiano no período de 24h, havendo a necessidade de testar este efeito em um período prolongado. Os cimentos coloridos facilitaram a identificação e remoção do material que permaneceu sobre a estrutura dental, reduzindo o tempo de trabalho. / The advent of adhesion in dentistry allowed the use of orthodontic appliances directly cemented on the tooth surface. With these adhesive procedures, an important question about the most appropriate method for debond brackets and for wearing remnant bonding agents on dental enamel arises. There are several methods and instruments used for that purposes, but the literature indicates that, regardless of the technique, there is always damage to tooth structure. The use of orthodontic appliances associated with the excess bonding agent around the brackets allows a biofilm accumulation and thus caries development around accessories. This study aims to add colored metal methacrylates - copper and silver - on experimental orthodontic cement, and evaluate the influence of the color of new cements when identifying excesses prior to photoactivation of the product, and the remaining wear after debonding of accessories at the end of the treatment. Another objective was to evaluate the antimicrobial effect produced by the addition of methacrylates against Streptococcus mutans, a microorganism that is strongly associated to dental caries. The groups tested were experimental orthodontic cement without metal methacrylate (C), experimental orthodontic cement with Silver Methacrylate (CMAg), experimental orthodontic cement with Copper Methacrylate (CMCu) and commercial references - conventional orthodontic cement (TB - Transbond XT, 3M Unitek, Monrovia, CA, USA) and resin composed of distinct coloration of the dental structure (RZ250 - Filtek Z250 XT D3, 3M ESPE, St Paul, MN, USA). The materials were characterized as the degree of conversion, colorimetric properties, physical, chemical and mechanical properties, cell viability and antibacterial effect (through Agar Diffusion Method and Modified Direct Contact Test). The time used in cementing brackets and removal of the remnant bonding agent was evaluated, then the enamel surface was characterized by scanning electron microscopy (SEM), and the structural enamel loss resulting from the removal of the residual bonding agent was evaluated by means of 3D profilometry (surface roughness - Sa and volume of enamel loss - V). Experimental procedures of cementing, removal and wear of the remaining cement were performed by an experienced operator. For all tests it was considered p <0.05 as statistically significant. Through the tests, it was possible to identify that CMCu and CMAg can potentially be antimicrobial, since they showed inhibition zone larger than the other groups. CMCu inhibited microbial growth in the 24 hour period, needing to test this effect in a longer period. Colored cement facilitated the identification and removal of the material that remained on the tooth structure, reducing the working time.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpel.edu.br:prefix/3564 |
| Date | 27 July 2016 |
| Creators | Araújo , Raíssa Coi de |
| Contributors | 01315346028, http://lattes.cnpq.br/3857752875749027, Moraes, Rafael Ratto de, Michelon, Douver, Lima, Giana Silveira |
| Publisher | Universidade Federal de Pelotas, Programa de Pós-Graduação em Odontologia, UFPel, Brasil, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPEL, instname:Universidade Federal de Pelotas, instacron:UFPEL |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds