Orientador: Inez Valeria Pagotto Yoshida / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-12T12:33:20Z (GMT). No. of bitstreams: 1
Segatelli_MarianaGava_D.pdf: 6527296 bytes, checksum: 894b8cf377317b78d905bf778e5f743e (MD5)
Previous issue date: 2008 / Resumo: Este projeto envolveu a obtenção de materiais vítreos e/ou cerâmicos de SiCxOy e/ou SiC enriquecidos com carbono pela pirólise de precursores poliméricos híbridos, na presença e na ausência de acetato de níquel (NiAc). Os precursores poliméricos com e sem NiAc foram preparados por reação de hidrossililação entre poli(metilsiloxano) (PMS) e divinilbenzeno (DVB), em diferentes composições. Além destes precursores, nanotubos de carbono (NTC) foram incorporados ao precursor polimérico PMS/DVB e submetidos a um tratamento térmico a 1500°C em diferentes tempos. A estabilidade térmica e o rendimento cerâmico dos precursores foram analisados por TGA e a conversão polímero-cerâmica foi monitorada por XRD e espectros IR, C e Si NMR e Raman, além de análise elementar e medidas de densidade. A porosidade e a morfologia destes materiais também foram avaliadas. A composição do precursor polimérico influenciou a quantidade de carbono total nas cerâmicas resultantes, aumentando com a quantidade de DVB incorporada no precursor. O efeito da composição foi mais acentuado nas cerâmicas contendo Ni. Além disso, a incorporação de Ni aos precursores poliméricos promoveu alterações marcantes na estrutura e morfologia das cerâmicas, particularmente com relação à cristalização e a intensa carborredução, o que refletiu no aumento da densidade destes materiais devido à maior contribuição da fase cristalina b-SiC. A presença de Ni também contribuiu para a formação de nanofios retos e curvos contendo Si, O e C, principalmente na superfície dos corpos cerâmicos, apresentando diferentes composições em função de seus formatos. O aumento da temperatura de 950 a 1500°C favoreceu uma série de transformações estruturais nestes materiais, em especial, a organização da fase de Clivre dispersa na matriz cerâmica. A presença de NTC, como fonte extra de carbono, no precursor polimérico favoreceu a formação das fases de cristobalita e de b-SiC nas cerâmicas e o aumento da quantidade de defeitos na fase dispersa de Clivre. Para estas amostras, observou-se um processo de organização dos nanodomínios de carbono com o aumento do tempo de aquecimento a 1500°C, além de uma morfologia distinta das correspondentes cerâmicas obtidas na ausência dos NTC. / Abstract: In this study, vitreous and/or ceramic materials based on SiCxOy and/or SiC enriched with carbon were obtained by pyrolysis of hybrid polymeric precursors, in the presence or not of nickel acetate (NiAc). The polymeric precursors with and without NiAc were prepared by hydrosilylation reaction between poly(methylsiloxane) (PMS) and divinylbenzene (DVB), in different compositions. Apart from these precursors, carbon nanotubes (CNT) were added to the PMS/DVB precursor and submitted to thermal treatment at 1500°C in different times. The thermal stability and the ceramic yield of the precursors were analyzed by TGA and the polymer to ceramic conversion was monitored by XRD and IR, C and Si NMR and Raman spectra, elemental analysis and density measurements. The porosity and morphology of these materials were also evaluated. The polymeric precursor composition influenced the total carbon amount in the resulting ceramics, increasing with the DVB amount added to precursor. The effect of composition was more pronounced in the Ni-containing ceramics. In addition, the presence of Ni in the polymeric precursors promoted remarkable changes in the structure and morphology of the ceramics, particularly in relation to the crystallization and carboreduction, resulting in denser materials due to contribution of b-SiC crystalline phase. The introduction of Ni also contributed to the formation of straight and curved nanowires, mainly on the surface of the ceramic bodies, which presented different compositions according to their shapes. The increase of temperature from 950 to 1500°C promoted continuous structural transformations, leading to ordering process of Cfree phase dispersed in the ceramic matrix. The presence of CNT, used as an extra carbon source, in the polymeric precursor promoted the formation of cristobalite and b-SiC phases and the increase of defects in the Cfree phase presents in the ceramics. In the CNT-containing ceramics, the increase of the annealing time at 1500°C resulted in an ordering process of carbon nanodomains and a different morphology of the corresponding ceramics obtained without CNT. / Doutorado / Quimica Inorganica / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/250495 |
| Date | 10 July 2008 |
| Creators | Segatelli, Mariana Gava |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Yoshida, Inez Valéria Pagotto, 1950-, Radovanovic, Eduardo, Schiavon, Marco Antonio, Mazali, Italo Odone, Sígoli, Fernando Aparecido |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 105 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0027 seconds