Sintese de poli (esteres-uretanas) a base de poliois de poli (hidroxibutirato) e poli (caprolactona) / Synthesis of poly (ester-urethanes) from poly (hydroxybutyrate) and poly (caprolactone)

Orientador: Maria Isabel Felisberti / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-11T21:04:55Z (GMT). No. of bitstreams: 1
Alves_SabrinadeSousa_M.pdf: 1156094 bytes, checksum: 5b56bbbe834e47047d9d7c14d74333c1 (MD5)
Previous issue date: 2008 / Resumo: Materiais poliméricos com propriedades como biodegradabilidade e biocompatibilidade, como o poli(hidroxibutirato) (PHB) e a poli(caprolactona), vêm sendo amplamente estudados para aplicações com alto valor agregado, como a área biomédica. A síntese de poliuretanas contendo blocos de PHB e PCL visa a obtenção de um material que mantenha as características de biodegradabilidade e biocompatibilidade e que possua propriedades mecânicas diferentes dos materiais de partida, o que viabiliza um aumento na gama de aplicações destes polímeros. Neste trabalho, polióis de PHB e PCL com massa molar inferior a 6000 g mol foram obtidos através de reações de glicólise. Diferentes rotas e condições experimentais, utilizando diferentes solventes, catalisadores, tempo e temperatura, foram testadas para esta reação. A caracterização destes oligômeros foi feita através de análise de RMN H e C, DSC, TGA, índice de hidroxila e GPC. Na segunda etapa do trabalho, foram realizadas reações dos oligômeros obtidos com hexametileno diisocianato (HDI), um isocianato de cadeia linear de baixo poder carcinogênico. As estruturas químicas das poliuretanas obtidas nesta reação foram caracterizadas por FTIR e RMN H e C, as propriedades térmicas caracterizadas por DSC, TGA e DMA, físicas através de GPC e teste de solubilidade para verificar existência de reticulação / Abstract:The synthesis of polyurethanes containing PHB and PCL blocks aims to obtain materials with controlled mechanical properties maintain biodegradable and biocompatible polymers such as poly(hidroxybutyrate) (PHB) and poly(caprolactone) (PCL) have been largely studied. The synthesis of polyurethanes containing blocks of PHB and PCL aims to obtain materials with controlled mechanical properties maintaing the biodegradability and biocompatibility. In this work, polyols of PHB and PCL with molar weight less than 6000 g mol were obtained from glicolise reactions with ethylene glycol. The polyols were characterizated by RMN H e C, DSC, TGA, hydroxyl index and GPC. Diferent routes and experimental conditions, using diferent solvents, catalysts, time and temperature were tested. In a second step of this research reactions between the polyols and hexamethylene diisocianate (HDI), an alifatic isocianate with low carcinogenic toxicity were conduced in order to obtin polyurethanes. The chemical structure of polyurethanes obtained was characterized by FTIR and RMN H e C, thermal properties were characterized by DSC, TGA and DMA em physical properties by GPC and solubility test / Mestrado / Físico-Química / Mestre em Química

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248758
Date20 May 2008
CreatorsAlves, Sabrina de Sousa
ContributorsUNIVERSIDADE ESTADUAL DE CAMPINAS, Felisberti, Maria Isabel, 1959-, Lopes, Cristina Moniz Araujo, Gonçalves, Maria do Carmo
Publisher[s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Química
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Format82p. : il., application/pdf
Sourcereponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0025 seconds