Biodegradable Composites : Processing of thermoplastic polymers for medical applications.

Despite the recent development in PLA and PLGA based medical devices, there are still needs to further improve the mechanical performance of bioresorbable medical implants and their bioactivity. This is normally done by optimizing the filler compositions in selected groups ofbiodegradable polymer matrices. In this study, the effects of various filler levels on mechanical strength and thermal properties of PLA and PLGA composites were investigated. Composites containing different dosage of osteoconductive HAp with various particles size (0-5μm, 0-50 μm, nano size), β-TCP, bioactive glass and biodegradable Poly-L-lactide and Polylactide-glycolic acid was manufactured with melt blending, using a twin-screw extruder.The samples were investigated by Differential Scanning Calorimetry (DSC), thermo gravimetric analysis (TGA), Scanning Electron Microscopy (SEM), viscometer, three points bending machine, and Optical Microscopy (OM). The Extruder produced a porous profile. The result from TGA and SEM indicated that there was homogenous filler dispersion in the matrix after compounding.The result from DSC and Viscometer shows that there was some degradation duringcompounding. Mechanical properties of composites were modified by adding filler to matrix. The addition of Bioactive glass, as a filler, increases the degradation of the polymer matrix. The best filler that was applied is 0-5μm and nano HAp. Also in in-vitro degradation part of this thesis work, the effects of calcium phosphate materialsare investigated on degradation process.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:hb-19329
Date January 2009
CreatorsDamadzadeh, Behzad, Jabari, Hamideh
PublisherHögskolan i Borås, Institutionen Ingenjörshögskolan, Högskolan i Borås, Institutionen Ingenjörshögskolan, University of Borås/School of Engineering
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationMagisteruppsats,

Page generated in 0.0027 seconds