Orientador: Ângela Maria Moraes / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agrícola / Made available in DSpace on 2018-08-25T01:12:46Z (GMT). No. of bitstreams: 1
Souza_FernandaCarlaBombaldide_M.pdf: 2498035 bytes, checksum: f26cf0a46c0249d60c3316fd94c93e91 (MD5)
Previous issue date: 2014 / Resumo: A quitosana, a goma guar e a policaprolactona são exemplos de polímeros muito usados na obtenção de curativos para a terapia de lesões de pele devido ao fato de serem biocompatíveis e biodegradáveis. A fim de aumentar a atividade biológica destes curativos, a incorporação de compostos bioativos que estimulam o processo de cura das lesões pode ser feita. Neste contexto, este trabalho teve como objetivo a obtenção de curativos biologicamente ativos, por meio da incorporação do alfa-bisabolol, um composto antioxidante e anti-inflamatório de origem natural, a membranas constituídas de quitosana combinada com goma guar (Q-G) e de policaprolactona (PCL). Dois métodos de incorporação foram utilizados: adição direta do composto ativo à mistura polimérica (AD) e impregnação do composto nas membranas por imersão em solução etanólica (IE). As membranas produzidas foram caracterizadas quanto ao seu aspecto visual, cor e opacidade, morfologia, ângulo de contato com água, propriedades mecânicas e espessura em diferentes umidades, capacidade de absorção e perda de massa em etanol e em soluções aquosas, taxa de transmissão de vapor d¿água e espectro FTIR. A eficiência de incorporação do alfa-bisabolol às membranas e a atividade antioxidante deste composto foram determinadas, e sua cinética de liberação estudada. Os resultados mostraram que tanto os filmes de Q-G como de PCL apresentaram comportamento mais adequado para a aplicação no tratamento de lesões pouco exsudativas. As propriedades mecânicas dos filmes sofreram variação significativa apenas quando estes foram expostos a condições de umidade elevada. O alfa-bisabolol utilizado nos ensaios apresentou elevado grau de pureza, porém atividade antioxidante relativamente baixa. A inserção do composto na matriz ocasionou mudanças significativas em sua aparência e alterações em sua microestrutura. Para Q-G, baixas eficiências de incorporação foram obtidas, sendo o valor máximo atingido pelo método AD igual a 1,65%, o equivalente a 4,96 mg/g, enquanto que para o método IE atingiu-se cerca de 18%, com uma retenção de aproximadamente 1080 mg/g. Já no caso da PCL, alta eficiência de incorporação foi observada (100%). A liberação mostrou-se relativamente lenta em ambos os casos e a percentagem máxima de alfa-bisabolol liberado ficou em torno de 6% e 30%, o equivalente a 12 e 300 mg/g para filmes de PCL e de Q-G, respectivamente. O tempo prolongado de liberação permitiria a troca do curativo com intervalos de tempo maiores, tornando o tratamento menos incômodo para o paciente / Abstract: Chitosan, guar gum and polycaprolactone are polymers widely used to obtain wound dressings due to their biocompatibility and biodegradability. To increase the biological activity of these dressings, bioactive compounds which accelerate wound healing can be incorporated. In this context, this work aimed the development of biologically active dressings, through the incorporation of alpha-bisabolol, a natural antioxidant and anti-inflammatory compound, to membranes made of chitosan associated with guar gum (C-G) and of polycaprolactone (PCL). The incorporation of alpha-bisabolol was performed by two distinct methods: addition directly to the polymeric mixture (AD) and absorption of the active compound from an ethanolic solution (AS). The membranes were characterized regarding to visual appearance, color and opacity, morphology, water contact angle, water vapor transmission rate, swelling capacity in ethanol and in aqueous solutions as well as mass loss in the same media, strain at break, tensile strength and thickness in different humidities conditions and FTIR spectrum. Alpha-bisabolol incorporation efficiency and its antioxidant activity were determined and the release kinetics was studied. Results showed that both films are more suitable for the use in the treatment of lesions with low exudate levels. Mechanical properties suffered significant change only after exposure of the films to high humidity conditions. The alpha-bisabolol used in this study exhibits high purity, but relatively low antioxidant activity. The addition of the compound to the matrix led to significant changes in the appearance and to modifications in the microstructure of the films. The C-G membranes presented low incorporation efficiencies, with the maximum value of 1.65%, equivalent to 4.96 mg/g, for the AD method, and 18%, approximately 1080 mg/g, for the AS method. In the case of PCL, high incorporation efficiency (100%) was observed. The release of alpha-bisabolol from the matrices was relatively slow and the maximum percentage of compound released reached about 6% and 30%, equivalent to 12 and 300 mg/g for PCL and C-G films, respectively. A prolonged release would allow less frequent dressing changes, turning the treatment more comfortable for the patient / Mestrado / Engenharia Química / Mestra em Engenharia Química
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/266114 |
Date | 25 August 2018 |
Creators | Souza, Fernanda Carla Bombaldi de, 1989- |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Moraes, Ângela Maria, 1966-, Foglio, Mary Ann, Kieckbusch, Theo Guenter |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Química, Programa de Pós-Graduação em Engenharia Química |
Source Sets | IBICT Brazilian ETDs |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 123 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |