000854505.pdf: 8120690 bytes, checksum: eb782c5171f32dc120c86661117feec0 (MD5) / Neste trabalho, nanopartículas de TiO2 foram obtidas a partir de uma metodologia baseada no processo sol-gel seguido pelo método solvotérmico assistido por micro-ondas (SAM), em diferentes tempos de processamento. Os TiO2 foram caracterizado pelas técnicas de análise térmica termogravimetria/calorimetria diferencial exploratória (TG/DSC), difração de raios X (XRD), espectroscopia Raman, espectroscopia de ressonância paramagnética nuclear (EPR), espetroscopia de fotoelétrons excitados por raios X (XPS), microscopia eletrônica de varredura com canhão de elétrons por emissão de campo (FEG-SEM), espectroscopia de energia dispersiva (EDS), microscopia eletrônica de transmissão de alta resolução (HR-TEM). As análises da superfície e porosidade foram efetuadas a partir do método BET, enquanto que as propriedades ópticas foram investigadas pela espectroscopia de absorção óptica na região UV-Vis, espectroscopia de fotoluminescência (FL) e experimentos fotocatalíticos. As temperaturas de calcinação em 380 °C e 450 °C formaram um material cristalino heteroestruturado (anatase+bruquita) e monofásico (anatase), respectivamente. Porém, a curta distância, estes estão altamente ordenados pela presença somente dos modos vibracionais relativos à fase anatase ativos no Raman. Os resultados de FEG-SEM e HR-TEM relevaram que o TiO2 é um material policristalino formado por cristalitos (~10 nm) que crescem por meio de um mecanismo de coalescência orientada e aleatória, resultando em um aglomerado microscópico de nanopartículas. A presença de defeitos estruturais foi atribuída às vacâncias de oxigênios monoionizadas (VO•) pelos sinais de EPR em g ≈2,023 e g≈1,966, que de acordo com os resultados de XPS e EDS sugerem que estas vacâncias estão tanto no bulk quanto na superfície. A partir do refinamento Rietveld, as vacâncias de oxigênio foram interpretadas como desvios em... / In this work, TiO2 nanoparticles were obtained from methodology based on the sol-gel process followed by the microwave-assisted solvothermal method (MAS), in different processing times. The TiO2 were characterized by thermal analysis (TG/DSC), X-ray Diffraction (XRD), Raman spectroscopy, electron paramagnetic resonance (EPR), high-resolution transmission electron microscopy (HR-TEM), energy dispersive spectroscopy (EDS), X-ray Photoelectron spectroscopy (XPS). Porosity and surface analysis were performed from the Brunauer-Emmett-Teller (BET) method, while the optical properties were investigated by UV-Vis absorption spectroscopy, photoluminescence (PL) and photocatalytic experiments. The calcination temperatures at 380 °C and 450 °C were responsible by the heterostructured (anatase + bruquita) and the monophase (anatase) crystalline materials, respectively. However, at short range are highly ordered due the presence of vibrational modes ascribed to only anatase phase active in Raman. The FEG-SEM e HR-TEM results showed TiO2is a polycrystalline material consisting of nanocrystals (~10 nm) grow up by means of the Oriented attachment mechanism, resulting in a microscopic agglomeration of nanoparticles. The presence of structural defects was attributed to singly ionized oxygen vacancies (VO•) by EPR signals at g≈2,023 and g≈1,966, which according to XPS and EDS results, suggest that these vacancies are in both bulk and surface. From the Rietveld refinement, the oxygen vacancies were interpreted as deviations from (Ti−O) and (O−T̂i−O), which tend to turn the ordered [TiO6] clusters in complex clusters [TiO5.VOx], [TiO5.VO•] and [TiO5.VO••]. The decreasing in the optical band gap (2,68-2,99 eV) and the PL at room temperature, indicate that these complex clusters represent the defects responsible for disorder at medium-range which exhibit a broadband at visible (350-700 nm) and another...
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/136092 |
Date | 04 August 2015 |
Creators | Silva Junior, Eurípedes [UNESP] |
Contributors | Universidade Estadual Paulista (UNESP), Silva, Elson Longo da [UNESP] |
Publisher | Universidade Estadual Paulista (UNESP) |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 225 f. : il. - |
Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
Rights | info:eu-repo/semantics/openAccess |
Relation | -1, -1 |
Page generated in 0.003 seconds