Highly proton conducting polymers for operation in hydrogen/oxygen proton exchange membrane fuel cells (PEMFCs) provide often a poor mechanical strength due to high water contents. To strengthen the conducting polymers, blends with different ratios of partially fluorinated sulfonic acid graft and diblock copolymers with perfluorinated polymers were prepared. To analyze the effect of the different quantities of the compounds, with regard to water sorption and proton conducting properties, membranes were prepared by dissolving the components and drop casting.
Partially sulfonated poly([vinylidene difluoride-co-chlorotrifluoroethylene]-g-styrene) (P(VDF-co-CTFE)-g-SPS) was blended with polyvinylidene difluoride (PVDF), decreasing the ion exchange capacity (IEC). The blended polymers absorbed less water. However, the by AC impedance spectroscopy determined proton conductivity stayed stable or increased slightly. The effective proton mobility remained constant. Partially sulfonated poly([vinylidene difluoride-co-hexafluoropropylene]-b-styrene) (P(VDF-co-HFP)-b-SPS) with two different PS-block lengths were blended with different amounts of poly(vinylidene difluoride-co-hexafluoropropylene) (P(VDF-co-HFP)). In that case, the polymers absorbed less water and the proton conductivity decreased stepwise by adding more than 20 wt% P(VDF-co-HFP). The results indicate that a blending of P(VDF-co-CTFE)-g-SPS with PVDF inhibits swelling without having an effect on the proton conductivity, though water sorption and IEC are reduced.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:ch1-qucosa-61695 |
| Date | 20 October 2010 |
| Creators | Weißbach, Thomas |
| Contributors | TU Chemnitz, Fakultät für Naturwissenschaften, Prof. Dr. Werner A. Goedel, Prof. Dr. Werner A. Goedel, Prof. Dr. Steven Holdcroft |
| Publisher | Universitätsbibliothek Chemnitz |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:masterThesis |
| Format | application/pdf, text/plain, application/zip |
Page generated in 0.0028 seconds