Dissertação (mestrado)—Universidade de Brasília, Faculdade UnB Gama, Programa de Pós-Graduação em Integridade de Materiais da Engenharia, 2016. / Submitted by Camila Duarte (camiladias@bce.unb.br) on 2017-02-02T17:00:28Z
No. of bitstreams: 1
2016_NiloJoséLimadaSilvaBrandão.pdf: 2624080 bytes, checksum: 49da07484afd1d134a7e07ebc01d7d09 (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2017-02-16T16:26:08Z (GMT) No. of bitstreams: 1
2016_NiloJoséLimadaSilvaBrandão.pdf: 2624080 bytes, checksum: 49da07484afd1d134a7e07ebc01d7d09 (MD5) / Made available in DSpace on 2017-02-16T16:26:08Z (GMT). No. of bitstreams: 1
2016_NiloJoséLimadaSilvaBrandão.pdf: 2624080 bytes, checksum: 49da07484afd1d134a7e07ebc01d7d09 (MD5) / As ligas com memória de forma possuem a capacidade de recuperar sua forma original após deformações severas. No comportamento pseudoelástico a liga possui capacidade dissipativa de energia, em decorrência do laço de histerese. Com o objetivo de conhecer a influência das temperaturas de envelhecimento na histerese de ligas de NiTi, adotou-se como metodologia a fabricação de molas helicoidais feitas com um fio comercial de NiTi com composição em peso de aproximadamente 56% de níquel e 44% de titânio, diâmetro de 2,16 mm e microestrutura em fase austenítica. Os corpos de prova (molas) passaram por tratamento térmico de 500 °C para alívio de tensão e foram envelhecidos nas temperaturas de 350 °C, 450 °C, 550 °C e 600 °C com isoterma de 30 minutos e têmpera em água. As molas foram ensaiadas mecanicamente para obtenção dos gráficos de histerese e caracterizadas por calorimetria exploratória diferencial (DSC), difração de raio X (DRX) e ensaios de microdureza vickers. O tratamento térmico de alívio de tensão (500 °C) e os envelhecimentos de 350 °C, 450 °C e 550 °C desenvolveram fase R. As temperaturas de transformação martensítica diminuíram para todas as amostras tratadas termicamente. Os tratamentos térmicos reduziram o valor da microdureza nas amostras quando comparadas à liga como recebida. Os tratamentos de envelhecimento de 350 °C e 450 °C em temperatura ambiente apresentam fase austenita, fase R e precipitação Ni2Ti. O envelhecimento de 350 °C aparentemente apresentou menor laço de histerese e o tratamento térmico de 500 °C o maior laço de histerese quando comparados todos os tratamentos. / The shape memory alloys have the ability to recover the original form, after large deformations. In pseudoelasticity, the alloy having energy dissipation capacity, as a result of the hysteresis loop. The objective is to know the influence of aging temperatures on the mechanical properties of a NiTi pseudoelastic. Springs were made with commercial wire NiTi, with composition 54% of Ni and 42 % of Ti, diameter 2.16 mm and austenitic microstructure. The springs had heat treatment for stress relief (500 °C), posteriorly the samples were heat-aging treatment at temperatures of 350 °C, 450 °C, 550 °C and 600 °C. The springs underwent mechanical testing, DSC, RXD, vickers microhardness. The aging treatment of 350 ° C, 450 ° C, 500 ° C and 550 ° C developed R phase. Heat treatment reduced the hardness of the samples. The martensitic transformation temperatures decreased for all thermally treated samples. The aging treatments of 350 °C and 450 °C at ambient temperature exhibit in their austenite phase, R phase and Ni2Ti precipitation. The aging treatment of 350 ° C apparently showed smallest hysteresis loop and heat treatment of 500 ° C the largest hysteresis loop when comparing with the all treatments.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/22619 |
| Date | 01 December 2016 |
| Creators | Brandão, Nilo José Lima da Silva |
| Contributors | Muterlle, Palloma Vieira |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data., info:eu-repo/semantics/openAccess |
Page generated in 0.0138 seconds