<p>This thesis is concerned with kinetic characterisation of theinsertion compound LiMn2O4, which is used as positive electrodematerial in rechargeable lithium batteries. Three different typesof electrode configurations have been investigated, namely singleparticles, thin films and composite electrodes. Differentelectrochemical techniques, i.e. linear sweep voltammetry (LSV),electrochemical impedance spectroscopy (EIS), potential step, andgalvanostatic experiments were applied under various experimentalconditions. The majority of the experimental data were analysedby relevant mathematical models used for describing the reactionsteps of insertion compounds.</p><p>It was concluded that a model based on interfacialcharge-transfer, solid-phase diffusion and an external iR-dropcould be fairly well fitted to LSV data measured on a singleelectrode system over a narrow range of sweep rates. However, itwas also found that the fitted parameter values vary greatly withthe characteristic length and the sweep rate. This indicates thatthe physical description used is too simple for explaining theelectrochemical responses measured over a large range of chargeand discharge rates.</p><p>EIS was found to be a well-suited technique for separatingtime constants for different physical processes in the insertionand extraction reaction. It was demonstrated that the impedanceresponse is strongly dependent on the current collector used.According to the literature, reasonable values of theexchange-current density and solid-phase diffusion coefficientwere determined for various states-of-discharge, temperatures andelectrolyte compositions. Experiments were carried out in bothliquid and gel electrolytes. A method which improves thedistinction between the time constants related to thematerials intrinsic properties and possible porous effectsis presented. The method was applied to composite electrodes.This method utilises, in addition to the impedance responsemeasured in front of the electrode, also the impedance measuredat the backside of the electrode.</p><p>Finally, the kinetics of a composite electrode was alsoinvestigated by in situ X-ray diffraction (in situ XRD) incombination with galvanostatic and potentiostatic experiments. Noevidence of lithium concentration gradients could be observedfrom XRD data, even at the highest rate applied (i.e. ~6C), thusexcluding solid-phase diffusion and also phase-boundary movement,as described by Ficks law, as the ratelimiting step.</p><p><b>Key words:</b>linear sweep voltammetry, electrochemicalimpedance spectroscopy, potential step, in situ X-raydiffraction, microelectrodes, electrode kinetics, LiMn2O4cathode, rechargeable lithium batteries</p>
| Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:kth-3429 |
| Date | January 2002 |
| Creators | Hjelm, Anna-Karin |
| Publisher | KTH, Chemical Engineering and Technology, Stockholm : Kemiteknik |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, text |
| Relation | Trita-KET, 1104-3466 ; 162 |
Page generated in 0.0019 seconds