Orientadores: Antonio Jose Ramirez Londono, Paulo Roberto Mei / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-20T04:14:39Z (GMT). No. of bitstreams: 1
Hermenegildo_TahianaFranciscadaConceicao_D.pdf: 6825596 bytes, checksum: 036996ce1577dccad9ce590969e2cfe2 (MD5)
Previous issue date: 2012 / Resumo: Neste trabalho chapas do aço ISO 3183 X80M, foram soldadas empregando o processo de soldagem por atrito com pino não consumível, conhecido em inglês como ''Friction Stir Welding'', através de dois passes, sendo um em cada lado da chapa, utilizando ferramentas de NBCP (Nitreto de Boro Cúbico Policristalino). Juntas soldadas com aportes térmicos diferenciados foram processadas para estudo visando entender a influência da velocidade rotacional e de soldagem nas transformações microestruturais e no desempenho mecânico das juntas. Para tal, foram utilizadas as técnicas de microscopias óptica e eletrônica de varredura e transmissão, EBSD (Electron Backscattering Diffraction) e difração de raios-X para caracterização microestrutural. A determinação da história térmica, juntamente com ensaios mecânicos de microdureza, tração, dobramento e tenacidade à fratura (CTOD) complementaram a avaliação das juntas. Pelas análises microestruturais realizadas nas juntas de menor e maior aporte térmico e com o auxílio da história térmica, ficaram evidenciados os efeitos da deformação abaixo e acima da temperatura de não recristalização, da taxa de resfriamento e da recristalização dinâmica e metadinâmica na evolução microestrutural da zona misturada. Ensaios de dureza por microindentação Vickers e de tenacidade à fratura revelaram que a junta produzida com menor aporte térmico apresentou menor dureza e maior tenacidade na zona misturada. Por outro lado, a dureza e a tenacidade da zona afetada pelo calor não foram influenciadas pela variação dos parâmetros adotados neste trabalho. Os ensaios de dobramento não revelaram quaisquer descontinuidades nos corpos de prova, enquanto que nos ensaios de tração as amostras romperam sempre no metal de base, indicando uma alta resistência mecânica da junta soldada quando comparado ao metal de base. Tais resultados combinados validam completamente as juntas soldadas por SAPNC em relação às normas vigentes para a sua aplicação. As características microestruturais corroboram com o desempenho mecânico das juntas avaliadas / Abstract: In this work X80M ISO 3183 steel plates were welded using the Friction Stir Welding process by two passes, one on each side of the plate using PCBN (Polycrystalline Cubic Boron Nitride) tools. To understand the influence of the rotational and welding speed on the microstructural evolution and mechanical performance of the welded joints, samples with different heat inputs were processed. To this end, optical, scanning and transmission electron microscopy, EBSD (Electron Backscattering Diffraction), X-ray diffraction were used for the microstructural characterization. The thermal history registration with the mechanical tests of microhardness, tensile, bending and fracture toughness (CTOD) completed the evaluation of the joints. Based on the microstructural characterization and thermal history analyses of the joints with lower and higher heat input, the effects of deformation below and above the non-recrystallization temperature, cooling rate, and dynamic and metadynamic recrystallization on the microestrutural evolution of the stir zone were evidenced. Vickers microhardness and fracture toughness tests showed that the joint produced with lower heat input has lower hardness and higher toughness within the stir zone. Moreover, the hardness and toughness of the heat affected zone were not influenced by the parameters variation adopted in this work. The bending test did not revealed discontinuities in the specimens, while the tensile test specimens failed within the base metal, indicating a higher resistance of the weld metal when compared to the base metal. Such combined results fully validate the FSW joints regarding its commercial application. The microstructural observations are in agreement with the mechanical performance of the joints / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263423 |
| Date | 20 August 2018 |
| Creators | Hermenegildo, Tahiana Francisca da Conceição |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Mei, Paulo Roberto, 1953-, Ramirez Londono, Antonio José, Londono, Antonio Jose Ramirez, Fogagnolo, João Batista, Button, Sergio Tonini, Gorni, Antonio Augusto, Batalha, Gilmar Ferreira |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 159 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds