Previous issue date: 2017-06-28 / O polissacarídeo goma xantana (GX) tem ganhado notável atenção e tem sido bastante estudado e frequentemente aplicado em formulações alimentícias, cosméticas, farmacêuticas, e até mesmo na indústria petrolífera. Com o objetivo de explorar ainda mais as funções desse polissacarídeo, muitos estudos têm se concentrado em verificar os efeitos de diversos tratamentos físicos e químicos, na relação estrutura-propriedades técnico-funcionais. Um dos tratamentos aplicados, vem sendo a adição de eletrólitos para mudar a força iônica do meio, que consiste no foco de estudo do presente trabalho de pesquisa. Em este estudo se pretendeu determinar as características físico-químicas e perfil reológico, de dispersões aquosas de goma xantana contendo sais de qualidade alimentar (NaCl, KCl, MgCl 2 e CaCl 2 ) em concentrações calculadas de modo a se obter diferentes forças iônicas (50 mM e 100 mM). No estudo, foi determinado o efeito da blindagem eletrostática dos cations dos sais, nas cargas elétricas das cadeias da goma xantana, o que foi verificado pela diminuição em modulo da grandeza potencial zeta. Também em termos estruturais, foram identificadas duas distribuições de tamanho de partículas de goma xantana, cuja polidispersidade ou grau de heterogeneidade foi ligeiramente incrementado pela presença de sais divalentes (MgCl 2 e CaCl 2 ). Esses aspetos estruturais geraram mudanças nos parâmetros reológicos avaliados para as dispersões. Especificamente, a viscosidade aparente foi ligeiramente diminuída para as dispersões contendo sais com cátions de maior raio atômico (K + e Ca 2+ ). O comportamento viscoelástico foi afetado pelos sais adicionados na maior força iônica (100 mM), sendo determinada a dispersão com a estrutura de um sólido elástico. Assim, o estudo pôde contribuir para se discutir e se compreender melhor como interações entre cadeias de goma xantana e diferentes cátions em meios aquosos levam a mudanças nas características reológicas desses meios. / Xanthan gum (XG) has received great attention, extensively studied and often applied in food, cosmetic, pharmaceutical formulations, and even in the oil industry. In order to further explore techno-functionalities of this polysaccharide, some studies have focused on verifying the effects of physical and chemical modifications on XG structure-function relationships. One of such modifications is the addition of electrolytes to change the ionic strength of the medium, which is the study focus of this research work. Here, we aimed to determine physicochemical and rheological characteristics of aqueous dispersions of XG, containing food grade salts (NaCl, KCl, MgCl 2 and CaCl 2 ) at concentrations adequately chosen to obtain different ionic strengths (50 mM and 100 mM). The electrostatic shielding effect of salts cations on the electrical charges of the XG chains was evaluated through zeta potential analyses. Also, in structural terms, two size distributions of XG particles were identified, whose polydispersity or degree of heterogeneity was slightly increased by the presence of salts formed by bivalent cations (MgCl 2 and CaCl 2 ). These structural aspects generated changes in the rheological parameters evaluated for the dispersions. Specifically, the apparent viscosity was slightly decreased for the dispersions containing salts with cations of greater atomic radius (K + and Ca 2+ ). The viscoelastic behavior was affected by the salts added at the highest ionic strength (100 mM). In such media, the material behaved as an elastic solid. From the study, it was interesting to have identified which characteristics of the salts present were preponderant in the generation of changes in the properties of XG dispersions. In this way, this study contributed to discuss and to understand how interactions between XG chains and different cations in aqueous media engender changes in rheological characteristics of such media.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:123456789/12993 |
| Date | 28 June 2017 |
| Creators | Nieto Galván, Zoila Rosa |
| Contributors | Ramos, Afonso Mota, Coimbra, Jane Sélia dos Reis, Oliveira, Eduardo Basílio de |
| Publisher | Universidade Federal de Viçosa |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFV, instname:Universidade Federal de Viçosa, instacron:UFV |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds