Corrosion behaviour of fly ash-reinforced aluminum-magnesium alloy A535 composites

The corrosion behaviour of cast Al-Mg alloy A535 and its composites containing 10 wt.% and 15 wt.% fly ash, and 10 wt.% hybrid reinforcement (5 wt.% fly ash + 5 wt.% SiC) was investigated using weight-loss and electrochemical corrosion tests, optical microscopy, Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). The tests were conducted in fresh water collected from the South Saskatchewan River and 3.5 wt.% NaCl solution at room temperature. The pH of the salt solution varied from 3 to 9. For comparison, two other aluminum alloys, AA2618 and AA5083-H116, were tested in the same electrolytes.
The results of the weight-loss corrosion test showed that unreinforced A535 alloy had a lower corrosion rate in fresh water and seawater environments than the composites at all the tested pH values. The corrosion rate of the composites increased with increasing fly ash content. As expected, the corrosion rates of A535 alloy and the composites tested in fresh water were lower than those in salt solution.
The results of the potentiodynamic and cyclic polarization electrochemical tests showed that the corrosion potential (Ecorr) and pitting potential (Epit) of the alloy were more positive than those of the composites. The corrosion and pitting potentials of the composites became more negative (active) with increasing fly ash content. The composites showed more positive (noble) repassivation or protection potential (Erp) than the matrix alloy, with the positivity increasing with fly ash content. Analysis of the electrochemical noise data showed that pitting corrosion was the dominant mode of corrosion for the alloy in 3.5 wt.% NaCl solution. Optical microscopy and SEM revealed that Mg2Si phase and Al-Mg intermetallics corroded preferentially to the matrix. The EDS data indicated that the protective oxide film formed on A535 contained Al2O3 and MgO.

Identiferoai:union.ndltd.org:USASK/oai:usask.ca:etd-09222008-235440
Date30 September 2008
CreatorsObi, Emenike Raymond
ContributorsSammynaiken, Ramaswami, Oguocha, Ikechukwuka N., Evitts, Richard W., Yang, Qiaoqin
PublisherUniversity of Saskatchewan
Source SetsUniversity of Saskatchewan Library
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://library.usask.ca/theses/available/etd-09222008-235440/
Rightsunrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report.

Page generated in 0.0022 seconds