Submitted by Ivone Costa (mivone@ufpa.br) on 2018-09-05T13:21:33Z
No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_SubstituicaoParcialCimento.pdf: 4365332 bytes, checksum: a4a823a2e150b352c2acaa92372c8496 (MD5) / Approved for entry into archive by Ivone Costa (mivone@ufpa.br) on 2018-09-05T13:22:03Z (GMT) No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_SubstituicaoParcialCimento.pdf: 4365332 bytes, checksum: a4a823a2e150b352c2acaa92372c8496 (MD5) / Made available in DSpace on 2018-09-05T13:22:03Z (GMT). No. of bitstreams: 2
license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)
Dissertacao_SubstituicaoParcialCimento.pdf: 4365332 bytes, checksum: a4a823a2e150b352c2acaa92372c8496 (MD5)
Previous issue date: 2018-06-28 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A substituição parcial do cimento Portland por resíduos industriais ou materiais de
origem natural com fonte renovável é um meio que já vem sendo utilizado para minimizar
os impactos ambientais gerados durante sua fabricação, tais quais a emissão de CO2, alto
gasto energético e exploração das jazidas de calcário. A substituição parcial desse
aglomerante pode melhorar, ainda, certas propriedades de concretos e argamassas e reduzir
o custo de produção. Nesse contexto, o bambu surge como um material com potencial para
utilização de suas cinzas em substituição parcial ao cimento Portland, como adição mineral
do tipo pozolânica, por ser um material natural com fonte renovável e rápido crescimento.
Diante disso, o objetivo desse trabalho é avaliar a utilização de cinzas do colmo do bambu
(Bambusa Vulgaris) como substituição parcial do cimento Portland. Para tal foram
produzidas cinzas do colmo do bambu em três temperaturas de calcinação: 500ºC, 600ºC e
700ºC. A cinza produzida a 600ºC obteve índice de desempenho com o cimento Portland
aos 28 dias superior ao estabelecido pela NBR 12653 (ABNT, 2014). Avaliou-se a
hidratação do cimento Portland parcialmente substituído por essa cinza, em proporções de
0%, 6%, 10% e 14% e foi constatado a diminuição da concentração de hidróxido de cálcio,
sendo mais expressiva com a incorporação de 10% de cinzas. Argamassas com as mesmas
proporções de substituição foram avaliadas no estado fresco e endurecido. A consistência
no estado fresco manteve-se constante, enquanto que a resistência à compressão, no estado
endurecido, sofreu acréscimo entre 10 e 15% com a adição das cinzas. Portanto, foi
concluído que a substituição parcial do cimento Portland por cinzas do colmo do bambu
calcinadas a 600ºC apresentou benefícios às amostras estudadas, características de
materiais considerados pozolânicos. / The partial replacement of Portland cement for industrial waste or materials of
natural origin with renewable source is a way that has already been used to minimize the
environmental impacts generated during its manufacture, such as CO2 emission, high
energy expenditure and exploitation of the limestone deposits. The partial replacement of
this binder can further improve certain properties of concrete and mortars and reduce the
cost of their production. In this context, bamboo appears as a material with potential to use
its ashes in partial replacement to the Portland cement, because it’s a natural material with
renewable source and fast growth. Therefore, the objective of this paper is to evaluate the
use of bamboo stem ashes (Bambusa Vulgaris) as partial replacement of Portland cement.
For that, bamboo stem ashes were produced at three calcination temperatures: 500°C,
600°C and 700°C. The ashes produced at 600ºC obtained a performance index with
Portland cement at 28 days higher than that established by NBR 12653 (ABNT, 2014). It
was evaluated the hydration of the Portland cement partially substituted by this ash, in
proportions of 0, 6, 10 and 14% and it was verified the decrease of the concentration of
calcium hydroxide, being more expressive with the incorporation of 10% of ashes. Mortars
with the same replacement proportions were evaluated in the fresh and hardened state. The
consistency in the fresh state remained constant, while the compressive strength, in the
hardened state, increased between 10 and 15% with the addition of the ashes. Therefore, it
was concluded that the partial replacement of the Portland cement by bamboo stem ashes
calcined at 600ºC presented benefits to the studied samples, characteristic of pozzolanic
materials / UNAMA - Universidade da Amazônia
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/10188 |
| Date | 28 June 2018 |
| Creators | MENDONÇA, Marcelly de Figueiredo |
| Contributors | MACÊDO, Alcebíades Negrão |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Civil, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | 1 CD ROM, reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0023 seconds