Orientadores : Cecilia A. de Carvalho Zavaglia, Maurizio Ferrante / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-01T19:52:37Z (GMT). No. of bitstreams: 1
Bagnato_OsmarRoberto_D.pdf: 25124208 bytes, checksum: 1d8b18863e12cf63a1dc98919b6a4d5b (MD5)
Previous issue date: 2002 / Resumo: Na busca de processos alternativos de união entre metais e cerâmicas, destaca-se o processo de soldagem por difusão (diffusion bonding), utilizado em tecnologias de ponta no campo da indústria aeroespacial, eletroeletrônica, vácuo e de energia. O processo de soldagem por difusão consiste em manter os materiais a serem unidos, num contato íntimo sob carga, numa dada temperatura e num dado tempo, onde se obtém juntas soldadas de elevada resistência mecânica e confiabilidade. O objetivo desse trabalho é promover a união de componentes cerâmicos de alta alumina, utilizando um metal de ligação, no caso uma liga AlSi, de elevada dutilidade através da técnica de junção por difusão, pela otimização dos principais parâmetros de processo como temperatura, tempo e carga aplicada; tais juntas devem apresentar resistência mecânica elevada e repetibilidade de fabricação. Para produzir as juntas, construiu-se um forno a vácuo com os acessórios necessários para a realização da operações sob carga, a vácuo, em alta temperatura; a definição dos ensaios mecânicos para a caracterização da resistência mecânica, das juntas, dos corpos de prova e a caracterização microestrutural das interfaces. Trabalhou-se três níveis para cada variável considerada, sendo que os corpos de prova obtidos foram submetidos a ensaio de flexão em quatro pontos e os resultados discutidos em termos de estatística de Weibull; as interfaces e as superfícies de fratura foram estudadas por técnicas de microscopia eletrônica de varredura e microanálise. Os resultados obtidos nos ensaios mecânicos indicaram grande variação em função das variáveis de processo, sendo que os melhores resultados se equiparam com os valores da cerâmica monolítica, da ordem de 340 MPa, obtidas nas condições de elevada e baixa temperatura, em tempos longos e curtos (90 e 20 minutos) e os piores resultados estão na faixa de 40 MPa, obtidos em tempos e temperaturas intermediários (60 minutos e 550 °C). Observou-se diferentes modos de fratura, sendo que nas temperaturas elevadas foram identificou-se características de fratura frágil e em temperaturas baixas e médias, fratura dutil. As técnicas de investigação microestrutural revelaram a presença de uma fase descontínua na interface metal-cerâmica nas amostras de baixa resistência mecânica, podendo muito provavelmente, estar associadas com as condições de processo, provocando a fragilização da junta. As interfaces de alta resistência se mostraram contínuas e sem defeitos / Abstract: Of the alternative processes utilized for joining metals and ceramics, one of the most relevant techniques is diffusion bonding, which is being used in high-technology applications in aerospace, electro-electronics, vacuum and energy industries. Diffusion-bonding processes consist of maintaining the materials to be joined in intimate contact under external pressure and controlled temperature, during a determined period of time. In this situation, it is possible to obtain high mechanical resistance and reliably welded joints. The objective of this work is to promote the joining of ceramic materials of high alumina, using a filler metal, in this case an AISi12 eutectic alloy with high ductility, using diffusion-bonding techniques, optimizing the main parameters of the process: temperature, time and pressure. The joints obtained by this process have high mechanical resistance and repetibily in fabrication. To make these joints, a vacuum furnace was developed with all the accessories to make joints under external pressure and high vacuum at high temperature, mechanical tests were defined for the complete characterization of the joints and the project of the samples, were designed and the microstructural characterization of the materials and joints realized. Three levels for each variable were considered (temperature, time and pressure), and the joints obtained were submitted to a four-point flexural mechanical test; the results were discussed in terms of We bull¿s statistics. The interface and fracture surfaces were studied by scanning electron microscopy and microanalysis techniques. The mechanical results from the four-point flexural test showed great dispersion in function of the process variables. The best mechanical results for the joints were similar to the values of mechanical results for the monolithic ceramics, or 340 MPa, obtained in low and high temperature, at short and long periods of time. The worst results were in the range of 40 MPa, when intermediate times and temperatures were used. The interfaces presented two types of fracture: in the joints made at high temperatures, fragile fractures were observed whereas, in the samples obtained at low and medium temperatures, ductile fractures were identified. The microstructural observations showed the presence of a discontinuous phase in the metal-ceramic interface of low mechanical resistance samples, probability associated with the process conditions, which provoke the fragility of the joints. All the reliable and high mechanical resistance joints were continuous and without defects / Doutorado / Materiais e Porcessos / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/265040 |
| Date | 04 August 2002 |
| Creators | Bagnato, Osmar Roberto |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Ferrante, Maurizio, Zavaglia, Cecília Amélia de Carvalho, 1954-, Mei, Paulo Roberto, Filho, Pedro Iris Paulin, Costa, Adilson Rodrigues da, Gregolin, Jose Angelo R. |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 231p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds