This thesis presents results of the corrosion layers removal which could be found on the archaeological artefact surfaces. The low pressure low temperature plasma reduction was used for this purpose. Brass samples were chosen for this study. Two different ways have been used to form model corrosion layers. Several sets of corrosion layers were prepared in laboratory in two different corrosion atmospheres, namely ammonia atmosphere and atmosphere of hydrochloric acid. These samples were placed into desiccator. Small quantities of sand were added to some sets of samples so samples with sandy incrustation were prepared. The corrosion layers had been usually formed during four weeks. The second way, which was used to prepare model corrosion layer, was the natural corrosion in soil or compost. In this case, the corrosion layers had been formed approximately 2 years. The samples were treated in the low pressure (150 Pa) cylindrical Quartz reactor (90 cm long and 9.5 cm in diameter) with a pair of external copper electrodes connected via the matching network to a radiofrequency generator (13.56 MHz). The flows of working gases were set by independent mass flow controllers. Whole system was continuously pumped by the rotary oil pump which was separated from the discharge reactor by liquid nitrogen trap with aluminium chips eliminating dust and reactive species from the gas flow. Each sample was placed on a glass holder at the reactor center. Plasma was generated in pure hydrogen or in mixture of hydrogen and argon. Total flow of working gas was 50 sccm. Different ratios of gas mixture were tested, the ratio 30 sccm hydrogen and 20 sccm argon flows was the best. RF discharge was used in a continuous and pulsed regime. Pulsed mode was carried out with various duty cycle at the frequency of 1000 Hz. There were two ways of temperature monitoring. The sample temperature during the treatment was monitored by a K-type thermocouple installed inside the sample in the first case. Thermometer optical probe was connected to the sample surface by a small stainless plate and allowed continuous sample temperature monitoring in the second way. Safe object temperature for copper and copper alloys is 100–120 °C. To avoid exceeding this temperature, power control or the duty cycle in pulse mode were automatically controlled if thermometer optical probe was used. Plasma chemical treatment is based on generation of reactive atomic hydrogen in plasma discharge. The main reactions during reduction were reactions between oxygen and chloride contained in the corrosion layer and the hydrogen ions and neutral atoms generated in the plasma. These reactions create an unstable OH radical, which emits light in the region of 306–312 nm. This radiation was detected by the optical emission spectroscopy using Ocean Optics HR4000 spectrometer with 2400 gr/mm grating. Data obtained from this method were used to calculate rotational temperatures and integral intensity of OH radicals that were used for the process monitoring. Corrosion layer was not completely removed during the reduction, but due to the reactions which occur in the plasma corrosion layer became brittle and after plasma chemical treatment can be removed easily. The SEM-EDS material analyses were carried out before and after treatment of some samples. Some samples were analysed by XRD analysis. EDS analysis showed that amount of oxygen and chloride was decreased, mainly at 400 W pulse mode.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:234528 |
| Date | January 2015 |
| Creators | Řádková, Lucie |
| Contributors | Slavíček,, Pavel, Zahoran,, Miroslav, Krčma, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0491 seconds