Previous issue date: 2015 / A propriedade pozolânica do resÃduo industrial de lã de rocha (RWP), bem como sua incorporação em matrizes de cimento Portland foi analisada nesta pesquisa. A lã de rocha é um material isolante muito utilizado por diversas indústrias. Inicialmente caracterizou-se o resÃduo através das técnicas: difratometria de raios X (DRX), fluorescência de raios X (FRX), análise térmica de Calorimetria Diferencial de Varredura e Termogravimetria (DSC/TG) na amostra comercial e no resÃduo; classificação do resÃduo segundo NBR 10.004 (2004), moagem, granulometria a laser e massa especÃfica. Posteriormente, avaliou-se o potencial de atividade pozolânica do resÃduo moÃdo em 1 e 2 horas em pastas produzidas com RWP e hidróxido de cálcio, e identificou-se os compostos formados pela análise térmica (DSC/TG), (DRX) e Microscopia Eletrônica de Varredura (MEV) para as idades de 28 e 90 dias, também para efeitos comparativos executou-se o ensaio de acordo com a NBR 5752 (2014) - à ndice de atividade pozolânica Cimento Portland e NBR 15895 (2010) - Determinação do teor de hidróxido de cálcio fixado - Método Chapelle modificado. Os objetivos especÃficos desta pesquisa foram; caracterizar o resÃduo de lã de rocha com intenção de sua valorização como material pozolânico. Obter o Ãndice de atividade pozolânica para as duas curvas granulométricas do resÃduo em estudo. Investigar o efeito da substituição do cimento Portland por resÃduo de lã de rocha em argamassas. Pode-se concluir que, a utilização do resÃduo industrial de lã de rocha como material pozolânico não foi conclusiva, o resÃduo apresentou um potencial desenvolvimento de pozolanicidade em idade avançadas. No efeito fÃler a incorporação dos resÃduos de lã rocha trouxe efeitos benefÃcios, como aumento da resistência a compreensão. Os resultados encontrados mostram que o resÃduo de lã de rocha utilizado nesta pesquisa pode ser classificado como classe II A - não inerte (não perigoso), possui caracterÃstica de sólido amorfo e se enquadra como material pozolânico conforme estabelecido pela norma NBR 12653 (2014). Nas análises térmicas da amostra resÃduo e comercial, apresentou contaminação por ferro no resÃduo. A incorporação do resÃduo nas pastas de hidróxido de cálcio, e nas argamassas aumenta a resistência à compressão, esta propriedade melhorada é o resultado da estrutura densa obtida pelo efeito de enchimento realizado pelas partÃculas do resÃduo. Supostamente, os produtos da reação pozolânica começam a ser formados após 90 dias de idade conforme observações realizadas pelo MEV. O ensaio de Chapelle modificado não apresentou atividade pozolânica.<br> / Abstract : The pozzolanic property of industrial waste rock wool (RWP) as well as its incorporation in Portland cement was analyzed in this research. The rock wool is an insulating material widely used by several industries. Initially, the residue was characterized by the techniques: X-ray diffraction (XRD), X-ray fluorescence (XRF), thermal analysis Differential Scanning Calorimetry and Thermogravimetry (DSC/TG) in commercial sample and its residue; classification of waste according to NBR 10004 (2004), grinding, laser granulometry and specific weight. Subsequently, we assessed the potential ground waste pozzolanic activity in 1 and 2 hours on ground produced by RWP and calcium hydroxide, and identified the compounds formed by thermal analysis (DSC / TG), (XRD) and (MEV ) to the ages of 28 and 90 days. Also for comparative purposes, it was executed the test according to NBR 5752 (2014) - pozolância Portland cement activity level and NBR 15895 (2010) - Determination of fixed calcium hydroxide content - modified Chapelle method. The objectives specific of this research were; characterize the rock wool waste with intention of upgrading them pozzolanic material. Get the pozzolanic activity index for the two size distribution curves of the residue in the study. To investigate the effect of replacing Portland cement for rock wool waste in mortars. It can be concluded that the use of industrial waste rock wool as a pozzolanic material was not conclusive, the residue showed a potential development of advanced age pozzolanic. In effect fillers the incorporation of rock wool waste brought beneficial effects, such as increase the compressive strength. The results show that the rock wool waste used in this study can be classified as class II A - not inert (non-hazardous) has amorphous solid feature and fits as pozzolanic material as established by NBR 12653 (2014). In the thermal analysis of the sample waste and commercial, showed contamination with iron in the waste. The incorporation of the waste on calcium hydroxide pastes, mortars and increases the compressive strength of this improved property is the result of dense structure obtained by filling effect achieved by the particulate waste. Supposedly of the pozzolanic reaction products begin to be formed after 90 days of age, according to observations made by SEM. The modified Chapelle test showed no pozzolanic activity.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/162689 |
| Date | January 2015 |
| Creators | Medeiros, Maiara Goulart |
| Contributors | Universidade Federal de Santa Catarina, Castilhos Junior, Armando Borges de, Rocha, JanaÃde Cavalcante |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 124 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0029 seconds