The theoretical part of the thesis deals with the summary of material properties and testing parameters that influence SCG process. The experimental part is aimed on the comparison of different condition effects on the process of FNCT and PENT. Chosen temperatures for PENT were 70; 80 and 90 °C and the applied nominal stress 2,0; 2,4 and 2,8 MPa. In the case of FNCT the chosen temperatures were the same and the ligamental stress was 4 MPa for all used environments which were: water, Arkopal N110 solution and Dehyton PL solution. In addition, several experiments were measuered under applied nominal stresses 3; 4; 5; 6; 8 a 10 MPa and at 80 °C in Arkopal N110 solution. The morphology of crack surfaces was studied afterwards. The obtained data were used for evaluaion by a five parameter equation.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:401905 |
| Date | January 2019 |
| Creators | Patzelt, Petr |
| Contributors | Přikryl, Zdeněk, Petrůj, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds