Influência da aplicação de selantes de superfície na rugosidade de resinas compostas / Surface sealant application influence on the resin composite roughness.

Este estudo avaliou, in vitro, a influência da aplicação de quatro selantes de superfície na rugosidade de duas resinas compostas. Cinqüenta espécimes foram confeccionados e divididos em 10 grupos com 5 espécimes cada, em função da combinação entre resina composta e selante de superfície, sendo: G1. Controle Concept; G2. Concept + Fortify; G3. Concept + Biscover; G4. Concept + Lasting Touch; G5. Concept + Fill Glaze; G6. Controle Esthet X; G7. Esthet X + Fortify; G8. Esthet X + Biscover; G9. Esthet X + Lasting Touch; G10. Esthet X + Fill Glaze. Os espécimes foram confeccionados com uma matriz específica, em quatro incrementos, com dimensões internas de 15mmX4mmX5mm, sendo sua polimerização realizada com o aparelho de lâmpada halógena Curing Light 2500 (500mW/cm2) por 20s cada incremento. Em seguida, foram armazenados em água destilada à 37ºC e umidade absoluta de 100% por 24 horas. Após este período, os espécimes foram adaptados em uma Politriz Metalográfica e planificados com lixas de granulometria 320, 600 e a rugosidade inicial foi aferida. Para a mensuração da rugosidade, utilizou-se o rugosímetro Hommel Tester T1000 basic. Numa segunda fase, aplicaram-se os selantes de superfície, conforme recomendações do fabricante, e uma nova aferição da rugosidade superficial foi realizada. Para o teste de abrasão, os espécimes foram submetidos a 100.000 ciclos de escovação, seguido de nova mensuração da rugosidade. Em adição à rugosidade e com o objetivo de avaliar qualitativamente a superfície de alguns espécimes, a leitura em Microscopia Eletrônica de Varredura foi empregada. Os resultados foram submetidos aos testes ANOVA a 3 critérios e Tukey para comparações individuais entre os diferentes grupos (p<0,05). A aplicação do selante de superfície diminuiu a rugosidade superficial das resinas compostas testadas (G2=0,0727, G3=0,0147, G4=0,0307, G5=0,0253, G6=0,0960, G7=0,0173, G8=0,0333, G9=0,0480). A abrasão simulada aumentou a rugosidade superficial para todos os grupos, com exceção do Fortify (G2=0,0740, G7=0,0673) e Biscover (G7=0,0440), sendo os maiores valores apresentados pelo Lasting Touch (G4= 0,1253, G9=0,0980), seguido do Fill Glaze (G5=0,0933, G10= 0,0847). / This in vitro study evaluated the influence of the application of four surface sealers on the surface roughness of composite resins. Fifty specimens were divided into ten groups according to different patterns of composite resin and surface sealers, as follows: G1. Control with Concept resin; G2. Concept + Fortify; G3. Concept + Biscover; G4. Concept + Lasting Touch; G5. Concept + Fill Glaze; G6. Control with Esthet X; G7. Esthet X + Fortify; G8. Esthet X + Biscover; G9. Esthet X + Lasting Touch; G10. Esthet X + Fill Glaze. Specimens were made in four increments using a stainless steel matrix of 15x5x4mm and resin increments were polymerized with halogen lamp Curing Light 2500 (500mW/cm2) for 20 seconds each. After complete polymerization, specimens were stored in 100% humidity in distilled water at 37ºC for 24 hours. Following storage, specimens were polished using ascending grades (320, 600) of abrasive SiC paper under running water and the initial roughness was measured with a perfilometer Hommel Tester T100 basic (Hommelwerke GmbH ref. # 240851 - Schwenningem - Germany). Surface sealers were applied following the manufacturer\'s instructions and a new measurement of roughness was made. For the abrasive resistance test, specimens were submitted to 100.000 cycles of abrasive dentifrice brushing followed by surface roughness.. Qualitative analisys was made by using MEV. Results were submitted to Three-way ANOVA (p<0,05) and Tuckey\'s test to individual comparisons between different groups. Surface sealant application provided smoother surfaces for of composite resins tested (G2=0.0727, G3=0.0147, G4=0.0307, G5=0.0253, G6=0.0960, G7=0.0173, G8=0.0333, G9=0.0480). The abrasion test increased the surface roughness for all tested groups, except Fortify (G2=0,0740, G7=0,0673) and Biscover (G7=0,0440). Lasting Touch presented rougher surfaces (G4= 0,1253, G9=0,0980), followed by Fill Glaze (G5=0,0933, G10= 0,0847).

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-28052009-165339
Date27 March 2009
CreatorsFlávia Pardo Salata Nahsan
ContributorsRafael Francisco Lia Mondelli, Juan Carlos Castañeda Espinosa, Eduardo Batista Franco
PublisherUniversidade de São Paulo, Odontologia (Dentística), USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds