The dissertation thesis deals with the preparation and characterisation of a-CSi:H and a CSiO:H thin films prepared using the process of plasma enhanced chemical vapour deposition (PECVD). Tetravinylsilane (TVS) and its mixtures with argon and oxygen were used to deposit films on both planar substrates and fibre bundles. Main characterisation techniques were employed to study the topography of films, namely atomic force microscopy (AFM). Their mechanical properties were studied through nanoindentation; the nanoscratch test was used to assess the film adhesion to the substrate. Other analysed properties were internal stress and friction coefficient. The particular attention was paid to the work of adhesion and its determination. This knowledge was further applied to the preparation of surface treatments of glass fibres and, subsequently, polymer composites. Those were tested using the push-out test and the short beam shear test. Based on the results, the effects of deposition conditions and the relationships between the studied properties and quantities were determined.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:433414 |
| Date | January 2020 |
| Creators | Plichta, Tomáš |
| Contributors | Shukurov, Andrey, Klapetek, Petr, Čech, Vladimír |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds