The interaction between metal nanoparticles and small molecules has been investigated by FTIR and UV-visible absorption spectroscopy. Electrospray deposition into an argon matrix was chosen as the initial method. An electrospray metal source was tested in development stage. Both the formation of a stable corona discharge as well as a stable Taylor cone were successfully completed. Problems arose when the entire system was tested. It was determined that the vacuum was insufficient for the length of the flight path. Focus then shifted to nanoparticles in more conventional environments. Sol-gel encapsulated nanoparticles were generated, in the form of both monoliths as well as thin film coatings on silicon wafers. The gels were exposed to 1atm of carbon monoxide in a gas cell. The method encountered problems due to spectral interference from the matrix. The next attempt consisted of solution stabilized nanoparticles. The solution was exposed to various amounts of both ammonium sulphate and diethylamine. There was again the problem of solvent interference, even when attempting to observe the system using Raman spectroscopy. Finally, surface stabilized nanoparticles were generated, using 3-mercaptopropyltrimethoxysilane to adhere the particles to glass slides. While the coating was successfully applied to the glass slides, as confirmed with Raman spectroscopy, it was not possible to get the nanoparticles to adhere. Future outlook for this project is briefly reviewed. / Thesis (Master, Chemistry) -- Queen's University, 2009-06-26 10:30:58.295
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OKQ.1974/1973 |
Date | 26 June 2009 |
Creators | WEST, BRANDI |
Contributors | Queen's University (Kingston, Ont.). Theses (Queen's University (Kingston, Ont.)) |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English, English |
Detected Language | English |
Type | Thesis |
Format | 2181661 bytes, application/pdf |
Rights | This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner. |
Relation | Canadian theses |
Page generated in 0.0011 seconds