Thin film coatings of ZnO, TiO2, CeOX and BiOX have been deposited on soda lime silica glass through spray pyrolysis. The effects on the optical properties of the coated glass, as well as the possible impacts on the life expectancy and energy efficiency of PV-modules have been studied. ZnO and TiO2 coatings both reduced the transmission of UV radiation of wavelengths destructive to PV-modules. Therefore, both have the potential to increase the life expectancy of PV-modules if used on cover glass. The ZnO thin film also showed an increase in photoluminescence at 377 nm when radiated with UV radiation of 325 nm while TiO2 reduced the photoluminescence. ZnO coatings on the cover glass have the potential to increase the efficiency of PV-modules in addition to UV protection. No CeOX or BiOX films were found to be deposited with the method used. The ZnO and TiO2 coated samples showed a decrease in transmission of light, due to increased reflection and possibly scattering. This needs to be addressed if these kinds of coatings are going to be beneficial for Si PV-modules.
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:lnu-75044 |
Date | January 2018 |
Creators | Johansson, Wilhelm |
Publisher | Linnéuniversitetet, Institutionen för byggd miljö och energiteknik (BET) |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0038 seconds