AgÃncia Nacional do PetrÃleo / FundaÃÃo Cearense de Apoio ao Desenvolvimento Cientifico e TecnolÃgico / Os aÃos inoxidÃveis duplex possuem boas propriedades mecÃnicas e excelente resistÃncia à corrosÃo, aumentando seu uso em ambientes agressivos. Estas caracterÃsticas os fazem muito utilizados principalmente na indÃstria quÃmica e petroquÃmica. Geralmente, a fabricaÃÃo e reparo destes equipamentos envolvem operaÃÃes de soldagem, sendo que à muito importante avaliar a influÃncia dos parÃmetros de soldagem multipasse no balanceamento de fases, na microestrutura e microdureza. Primeiramente, foram realizadas soldagens em aÃo ASTM A516 Gr. 60 com eletrodo revestido AWS 2209-17, empregando diversas energias, variando a velocidade e corrente de soldagem. Foi feita a caracterizaÃÃo microestrutural atravÃs de microscopia Ãptica, quantificaÃÃo do teor de ferrita utilizando ferritoscÃpio e ensaio de microdureza para avaliar o metal de solda. Posteriormente, foram selecionadas as melhores condiÃÃes da etapa anterior para soldagem do aÃo inoxidÃvel duplex UNS S31803 para avaliar o efeito da energia de soldagem no balanceamento de fases, na microestrutura e microdureza no metal de solda e ZAC. Na Ãltima etapa foram realizadas soldagens em juntas de aÃo duplex, de modo a avaliar o efeito da energia de soldagem e restriÃÃo da junta no balanceamento de fases, microestrutura, microdureza e tenacidade do metal de solda e da ZAC. Foi verificada a influÃncia da energia de soldagem no teor de ferrita, possuindo comportamentos diferentes de acordo com os parÃmetros de soldagem. As microestruturas bÃsicas da austenita formada foram alotrimÃrfica, WidmanstÃtten e intragranular. Nas regiÃes com sobreposiÃÃo de passe houve maior quantidade de austenita no metal de solda e microestrutura mais refinada na ZAC. Foi observado que quanto maior a velocidade de soldagem, maior a quantidade de WidmanstÃtten. De forma geral, foi observado menor nÃvel de microdureza no metal de solda, principalmente nas condiÃÃes com maior quantidade de austenita WidmanstÃtten. A restriÃÃo da junta soldada influenciou no balanceamento de fases e na tenacidade da ZAC. NÃo houve efeito da energia de soldagem na tenacidade do metal de solda, possuindo nÃveis menores em relaÃÃo ao material como recebido / Duplex stainless steels show good mechanical properties and excellent corrosion resistance. These qualities are increasing their use in aggressive environments. Thus, these characteristics make them very used in chemical and petrochemical, mainly. Generally, the manufacture and repair of any industrial equipment involve welding operations, even though it is very important to evaluate the influence of multipass welding parameters in phase balances, microstructure and microhardness. Firstly, the shielded metal arc welding in steel ASTN A516 Gr. 60 with electrode AWS 2209-17 had been carried through with many energies, varying welding speed and current. Microstructural characterization by optic microscopy, quantification of ferrite content using ferritscope and microhardness test has being performed to evaluate the weld metal. After that, the best conditions of the last stage for welding of duplex stainless steel UNS S31803 had been chosen to evaluate the effect of the welding energy in phase balances, microstructure, and microhardness in the weld metal and HAZ. In the last stage, the weldings in joint of duplex steel had been carried through, in order to evaluate the effect of the welding energy and restriction of joint in phase balances, microstructure, microhardness and toughness of the weld metal and HAZ. The influence of the welding energy in the ferrite content was checked, although the behavior was different according to variation of the welding parameters. The basic microstructures of formed austenitic were allotriomoph, WidmanstÃtten and intragranular. Regions with pass overlapping presented greater amount of austenite in the weld metal and microstructure more refined in the HAZ. It was observed that increasing welding speed, greater is the amount of WidmanstÃtten austenite. In general, the increase of the amount of WidmanstÃtten austenite decreases level of microhardness in the weld metal. The restriction of the welded joint influenced in phase balances and toughness of the HAZ. There was not effect of the welding energy on toughness of the weld metal and this region occurred higher levels in relation to material as received
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:3000 |
| Date | 20 October 2009 |
| Creators | Everton Barbosa Nunes |
| Contributors | Marcelo Ferreira Motta, Hamilton Ferreira Gomes de Abreu, Jesualdo Pereira Farias, SÃrgio Souto Maior Tavares |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |