license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_EstudoTecnicaEnchimento.pdf: 2756317 bytes, checksum: 5368bbe5c167a43b3cf8052ad2645cf2 (MD5) / Made available in DSpace on 2014-06-23T02:13:36Z (GMT). No. of bitstreams: 2
license_rdf: 23898 bytes, checksum: e363e809996cf46ada20da1accfcd9c7 (MD5)
Dissertacao_EstudoTecnicaEnchimento.pdf: 2756317 bytes, checksum: 5368bbe5c167a43b3cf8052ad2645cf2 (MD5)
Previous issue date: 2011 / FAPESPA - Fundação Amazônia de Amparo a Estudos e Pesquisas / Nesse trabalho estudou-se a viabilidade operacional e as características econômicas e geométrica da técnica do processo de soldagem GMAW-CW (alimentação
adicional de um arame frio) em comparação Gas Metal Arc Welding (GMAW). O
sistema de alimentação de arame frio foi projetado e adaptado a pistola de soldagem
MIG/MAG. Utilizou-se uma fonte eletrônica de múltiplos processos ajustada em
tensão constante e CC+, a proteção gasosa foi uma mistura 75%Ar+25%CO2 e CO2
comercialmente puro. O arame utilizado foi o da classe ER70S-6 com diametro de
1,2 mm para o arame eletrodo e 1,0 mm para o arame frio, os dois arames foram
alimentados em cabeçotes independentes. As variáveis operacionais de entrada
foram: a velocidade de alimentação de arame energizado, em três níveis, 4, 6 e 8
m/min e a velocidade de alimentação do arame frio em 50%, 60% e 70% da
velocidade de alimentação do arame energizado. As soldagens foram automatizadas
em simples deposição no sentido empurrando e o posicionamento do arame frio, em
um único nível, Tandem em chanfro em “U” de chapas de aço ASTM 1020. As
variáveis de resposta utilizadas foram: inspeção superficial dos cordões; análise da
geometria (largura, penetração, reforço e diluição) da solda e econômicas (taxa de
fusão, taxa de deposição, rendimento e custo operacional). Os resultados indicaram
que para a análise superficial, com o uso do gás Ar25%CO2 a superfície dos cordões
mostraram-se mais homogêneas em relação ao CO2 e com menor índice de
salpicagem, para a análise das características econômicas, o processo GMAW-CW
sempre foi superior ao processo convencional, quanto aos custos operacionais o
processo convencional mostrou-se menor, porém não houve o preenchimento do
chanfro, o que ocorreu com a utilização do processo GMAW-CW. / In this work studied the operational viability and the characteristics economic and
geometric of technique of the process welding GMAW -CW (additional
alimentation of a cold wire) in comparison Gas Metal Arc Welding (GMAW). The
alimentation system of cold wire was designed and adapted to welding gun GMAW.
Used an electronic source of multiple processes adjusted in constant voltage and DC
+, the gas shield was a mixture 75% Ar+25% CO2 and commercially pure CO2. The
wire used was Class ER70S-6 with diameter of 1.2 mm for the electrode wire and 1.0
mm for the cold wire, the both wires were fed in heads independent. The input
operating variables were the feed speed of wire energized at three levels, 4, 6 and 8
m / min and the wire feed speed in cold 50%, 60% and 70% of the wire feed speed
energized . The welds were automated in simple deposited in the pushing direction
and the positioning of the cold wire in a single level, Tandem in chamfer "U" steel
plate ASTM 1020. The variables of response used were: superficial inspection of the
cords, analysis of the geometry (width, penetration, reinforcement and dilution) and
economic solder (melting rate, deposition rate, yield and operating cost). The results
indicated that for surface analysis, using the AR25% CO2 gas to the surface of the
strands were more homogeneous with respect to CO2 and less splash index for the
analysis of economic characteristics, the process always GMAW-CW was superior to
the conventional process, the operating costs the conventional process was lower,
but without filling of the chamfer, which occurred with the use of GMAW-CW.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufpa.br:2011/5107 |
| Date | January 2011 |
| Creators | BARBOZA FILHO, Lúcio da Silva |
| Contributors | BRAGA, Eduardo de Magalhães |
| Publisher | Universidade Federal do Pará, Programa de Pós-Graduação em Engenharia Mecânica, UFPA, Brasil, Instituto de Tecnologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UFPA, instname:Universidade Federal do Pará, instacron:UFPA |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0018 seconds