This diploma thesis is focused on preparation of perovskite methylammonium lead bromide thin film layers and also thin film layers of its precursors, namely methylammonium bromide and lead(II) bromide, by spin-coating from the solution; and optical characterisation of the prepared thin film layers by UV-VIS spectroscopy and spectroscopical ellipsometry. Methylammonium bromide does not absorb in visible nor ultraviolet region, the maximum absorption of lead(II) bromide occurred in ultraviolet region, methylammonium lead bromide absorbs in visible region. Optical band gaps were determined by Tauc method to (3,5 ± 0,1) eV for lead(II) bromide and 2,15 eV, respectively 2,25 eV for perovskite. Refractive indices and extinction coefficients were determined by ellipsometry in range of wavelengths from 290 nm to 830 nm and their dependence with layer thickness was discussed. Ellipsometry model used in this thesis consist on Tauc-Lorentz oscillators for methylammonium bromide, methylammonium lead bromide and partially for lead(II) bromide, which another part is formed by New Amorphous oscillator.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:445137 |
| Date | January 2021 |
| Creators | Rackovská, Anna Patrícia |
| Contributors | Schmiedová, Veronika, Zmeškal, Oldřich |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Slovak |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds