Localized Corrosion of FrictionStir Spot Welds in AZ31 Magnesium Alloys

A scanning reference electrode technique (SRET) apparatus has been designed and commissioned to investigate the corrosion of friction stir spot welds (FSSW) made in AZ31 magnesium alloys. The operational parameters of the apparatus have been calibrated to give good spatial resolution. By combining the SRET data with material flow data and immersion test data it was found that the FSSW process caused the formation of distinct noble and active regimes within the weld area. The noble region was aligned with the stir zone (SZ) and was caused by a dynamically recrystallized grain structure which is void of dislocations / twins, and β Mg17Al12. Localized corrosion attack was observed in both SRET and immersion testing along the thermo-mechanically affected zone (TMAZ). The same effect was consistently observed with a flat versus concave shoulder tool, and dwell times of 1s and 4s.

Identiferoai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OTU.1807/35538
Date04 July 2013
CreatorsJames, Andre
ContributorsNorth, Thomas H., Thorpe, Steven J.
Source SetsLibrary and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada
Languageen_ca
Detected LanguageEnglish
TypeThesis

Page generated in 0.0022 seconds