Avaliação da resistência adesiva e características da zircônia após diferentes tratamentos de superfície / Bond strength and surface characteristics evaluation of zirconia after different treatments

Submitted by Virgílio Vilas Bôas Fernandes Júnior (virgiliovilas@hotmail.com) on 2017-10-25T17:19:32Z
No. of bitstreams: 1
Tese FInal .pdf: 39214788 bytes, checksum: 9123d03a17e8efd22b18caf0276a31db (MD5) / Rejected by LUIZA DE MENEZES ROMANETTO (luizamenezes@reitoria.unesp.br), reason: Solicitado pelo autor. on 2017-10-25T18:25:54Z (GMT) / Submitted by Virgílio Vilas Bôas Fernandes Júnior (virgiliovilas@hotmail.com) on 2017-10-25T19:32:12Z
No. of bitstreams: 1
Tese Final pdf 3.pdf: 39239343 bytes, checksum: a57241186129e7ab3539248847265232 (MD5) / Approved for entry into archive by LUIZA DE MENEZES ROMANETTO (luizamenezes@reitoria.unesp.br) on 2017-10-30T17:58:25Z (GMT) No. of bitstreams: 1
fernandesjunior_vvb_dr_sjc.pdf: 39239343 bytes, checksum: a57241186129e7ab3539248847265232 (MD5) / Made available in DSpace on 2017-10-30T17:58:25Z (GMT). No. of bitstreams: 1
fernandesjunior_vvb_dr_sjc.pdf: 39239343 bytes, checksum: a57241186129e7ab3539248847265232 (MD5)
Previous issue date: 2017-09-01 / O objetivo desse estudo in vitro foi avaliar a resistência adesiva, rugosidade superficial, ângulo de contato e o espectro infravermelho da zircônia, após diferentes tratamentos de superfície. Para isso, blocos (n=9) de zircônia Y-TZP (e.max ZirCad - Ivoclar, Schann, Liechtenstein) foram seccionados em 39 fatias (12 x 11x 3 mm) divididas em grupos de acordo com cada teste. Para resistência adesiva, 20 fatias foram divididos em: 2 grupos controle; JAT, jateamento com óxido de alumínio e sílica + primer (Monobond Plus - Ivoclar, Schann, Liechtenstein); HFP, condicionamento com ácido fluorídrico 10% + primer, e 3 experimentais: PL, plasma (Plasma Não Térmico de Superfície - modelo SAP); PLP, plasma + primer; HFPLP, ácido fluorídrico + plasma + primer. Cada fatia de zircônia foi cimentada (Multilink N - Ivoclair, Schann, Liechtenstein) a um bloco pré-polimerizado de resina composta. Após a cimentação os espécimes foram seccionados, e 48 palitos com área adesiva de 1 mm2 foram obtidos em cada grupo para o ensaio de microtração (μTBS). Quatro outras fatias foram submetidas à análise de rugosidade superficial e 12 fatias submetidas à análise do ângulo de contato, após os seguintes tratamentos de superfície: sem tratamento (AV), aplicação de ácido fluorídrico a 10% (AHF), aplicação de plasma (AP) e jateamento (AJ), sendo que para o ângulo de contato foram feitas medições imediatamente após o tratamento, após 12 e 24 horas. Os resultados foram submetidos à análise estatística Anova e teste de Tukey a 5% (p< 0,05). Os espectros das ligações químicas da superfície da zircônia foram determinados em 3 outras amostras após as seguintes condições: sem tratamento (AV), jateamento (JAT) e aplicação de ácido fluorídrico 10% seguido da aplicação do plasma (AHFP). Em termos de adesão, não houve diferença estatística significante entre os grupos JAT e HFPLP, porém esses 2 foram estatisticamente superiores ao grupos HFP, PL e PLP. O jateamento demonstrou aumentar significantemente a rugosidade superficial em relação aos demais grupos. O plasma demonstrou diminuir o ângulo de contato da superfície da zircônia imediatamente e ao longo de 48 horas. / The purpose of this in vito study was to evaluate zirconia bond strength, surface roughness, contact angle and to mesure infrared spectrum after different surface treatments. Y-TZP zirconium (e.max ZirCAD - Ivoclair, Schann, Liechtenstein) blocks (n=9) were sliced into 36 discs (12 x 11 x 3 mm) and divided (n=4) into surface treatment groups as following: two control groups: JAT, airborneparticle abrasion and HFP, 10% hydrofluoric acid etching + primer (Monobond Plus - Ivoclair, Schann, Liechtenstein)application ,and three experimental groups: PL, non-thermal plasma (Surface Non-Thermal Plasma SAP model) application; PLP non-thermal plasma + primer application, and HFPLP, 10% hydrofluoric acid etching + non-thermal plasma + primer application. Each zirconia disk was cemented (Multilink N - Ivoclair, Schann, Liechtenstein) to a pre-polymerized resin block (Filtek Z350 - 3M, St Paul, MN, USA). After cementation the specimens were sectioned and 48 sticks with adhesive area of 1 mm2 obtained from each group for micro-tensile testing (μTBS). Four discs were submitted to surface roughness analysis and 12 discs to contact angle analysis, after the following surface treatments: no treatment (AV), 10% hydrofluoric acid etching (AHF), non-thermal plasma application (AP); and airborne- particle abrasion (AJ). The results were submitted to ANOVA and Tukey's test (p < 0.05). Zirconia surface chemical bonds spectrum was determined in infrared spectroscopy for three specimens after the conditions: no treatment; airborne- particle abrasion and hydrofluoric acid etching + non-thermal plasma application. The results showed no statistically significant differences between the groups JAT and HFPLP, but these two groups were statistically superior to HFP, PL and PLP. Airborne- particle abrasion resulted in a significant increase of surface roughness compared to the other groups. Non-thermal plasma was shown to decrease the contact angle of the surface, within 48 hours.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/152014
Date01 September 2017
CreatorsFernandes Júnior, Virgílio Vilas Boas [UNESP]
ContributorsUniversidade Estadual Paulista (UNESP), Huhtala, Maria Filomena Rocha Lima [UNESP]
PublisherUniversidade Estadual Paulista (UNESP)
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP
Rightsinfo:eu-repo/semantics/openAccess