Previous issue date: 2018-01-26 / O processo de fabricação de painéis MDF é muito dinâmico e a todo instante surgem novidades tecnológicas buscando não somente otimizar custos de processo, mas incrementar novas características ou melhorar a resistência mecânica e usinabilidade. As fibras de madeira de eucalipto e as resinas termofixas como a uréia-formaldeído desempenham papel importantíssimo no contexto industrial. Um grande número de pesquisas e estudos se direciona a aperfeiçoar os processos de fabricação por meio do aprimoramento da matéria-prima. Muitos materiais foram desenvolvidos e adicionados tanto as fibras como as resinas sendo muito comum a busca por melhorias na resistência mecânica nas chapas MDF. A resina MDI (metileno difenil diisocianato), por exemplo, possui muitas vantagens conhecidas como a isenção de emissão de formol e a alta resistência a água, porém, outras características relacionadas à interação química com a madeira são pouco estudadas. Nesse contexto tecnológico, o presente trabalho se dedicou ao uso das técnicas termoanalíticas TG/DTG-DTA e DSC para investigar e compreender melhor a interação química entre as fibras de madeira de eucalipto e as resinas sintéticas termofixas e por fim, sugerir melhorias ao processo produtivo buscando assim, reduzir custos de fabricação. Além das técnicas termogravimétricas, a espectroscopia vibracional de absorção na região infravermelho médio com transformada de Fourier também foi usada para auxiliar na proposta reacional de polimerização e principalmente na identificação da estrutura química dos produtos gerados. Investigou-se também o processo de polimerização térmica do monômero MDI bem como sua degradação térmica seguindo as recomendações do ICTAC. As curvas TG/DTG-DTA mostraram que a polimerização foi incompleta em todas as resinas indicando a necessidade de ajustes no processo. A proposta reacional para as resinas UF e MDI está de acordo com os dados das curvas TG e espectros de MIR. A partir da polimerização da resina MDI sugeriu-se a formação de carbodiimidas como produto final. Ao final da pesquisa, algumas melhorias foram propostas como o aumento da temperatura da prensa e a diminuição da concentração de resina visto que na situação atual, a polimerização é incompleta e deixa resíduos nas chapas MDF. Comprovou-se também que as chapas fora de especificação podem ser usadas como biomassa combustível nas caldeiras em substituição ao cavaco de eucalipto, pois liberam mais calor quando estão em combustão. / The process of manufacturing MDF panels is very dynamic and at every moment technological innovations are emerging, seeking not only to optimize process costs, but to increase new characteristics or improve mechanical strength and machinability. Eucalyptus wood fibers and thermoset resins such as urea-formaldehyde play a very important role in the industrial context. A great number of researches and studies are directed at perfecting the manufacturing processes through the improvement of the raw material. Many materials have been developed and added to both fibers and resins, and the search for improvements in mechanical strength in MDF sheets is very common. MDI resin (methylene diphenyl diisocyanate), for example, has many advantages known as formaldehyde emission exemption and high water resistance, but other characteristics related to the chemical interaction with wood are little studied. In this technological context, the present work was dedicated to the use of TG / DTG-DTA and DSC thermoanalytical techniques to investigate and better understand the chemical interaction between eucalyptus wood fibers and thermosetting synthetic resins and, finally, to suggest improvements to the production process thus seeking to reduce manufacturing costs. In addition to the thermogravimetric techniques, the vibrational absorption spectroscopy in the medium infrared region with Fourier transform was also used to aid in the polymerization reaction proposal and mainly in the identification of the chemical structure of the generated products. The thermal polymerization process of the MDI monomer as well as its thermal degradation following the recommendations of the ICTAC were also investigated. The TG / DTG-DTA curves showed that the polymerization was incomplete in all resins indicating the need for process adjustments. The reaction proposal for the UF and MDI resins is in agreement with the data of the TG curves and MIR spectra. From the polymerization of MDI resin the formation of carbodiimides was suggested as the final product. At the end of the research, some improvements were proposed, such as the increase in the temperature of the press and the decrease of the resin concentration, since in the current situation the polymerization is incomplete and leaves residues in the MDF sheets. It has also been proven that non-specification sheets can be used as biomass fuel in boilers instead of eucalyptus chips, as they release more heat when they are in combustion.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/153553 |
| Date | 26 January 2018 |
| Creators | Silva, José Eduardo Estevam da |
| Contributors | Universidade Estadual Paulista (UNESP), Bannach, Gilbert [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | 600, 600 |
Page generated in 0.0028 seconds