The present work covers the fabrication and electrical and magnetic investigation of LaNiO3- and LaMnO3- based superlattices (SL). In recent years, several interesting theoretical predictions have been made in these SLs, for example, Mott insulators, metal-insulator transitions, superconductivity, topological insulators, and Chern insulators. Motivated by the promising theoretical predictions, four kinds of SLs with different designed structures and orientations were systematically studied in this thesis. The samples were grown by pulsed laser deposition with in-situ reflection high-energy electron diffraction to monitor the two-dimensional layer-by-layer growth process. In order to ensure the high-quality of SLs, growth parameters were optimised. Characteristic methods like X-ray diffraction, atomic force microscopy, and transmission electron microscopy were used. These measurements proved the high-quality of the SLs and provided the basis for electrical and magnetic measurements.
The first studied SL is the (001)-oriented LaNiO3/LaAlO3 SL, which was predicted as a superconductor in theory. Temperature-dependent resistivity measurements revealed a metal-insulator transition by lowering the dimensionality of the LaNiO3 layers in the SLs from three dimensions to two dimensions. The second studied SL is the (111)-oriented LaNiO3/LaAlO3 SL, which was predicted as a topological insulator in theory. The polarity-controlled conductivity was observed and the intrinsic conductivity mechanisms were discussed by means of appropriate modeling. The third studied SL is LaMnO3/LaAlO3 SL, which was predicted as a Chern insulator in theory. By lowering the temperature, a paramagnetic-ferromagnetic phase transition and a thermal activated behavior were observed in the SLs. The last studied SL is the LaNiO3/LaMnO3 SL, in which an exchange bias effect was expected. The studies reveal the exchange bias exists in three kinds of SLs with different orientations.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:15-qucosa-224437 |
| Date | 09 May 2017 |
| Creators | Wei, Haoming |
| Contributors | Universität Leipzig, Fakultät für Physik und Geowissenschaften, Prof. Dr. Michael Lorenz, Prof. Dr. Regina Dittmann |
| Publisher | Universitätsbibliothek Leipzig |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis |
| Format | application/pdf |
Page generated in 0.0017 seconds