Orientador: Rubens Caram Junior, Sergio Gama / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-08-07T00:28:46Z (GMT). No. of bitstreams: 1
Pecanha_RockfellerMaciel_D.pdf: 3378865 bytes, checksum: f292a59197a7f7161feaac791fa60e86 (MD5)
Previous issue date: 2006 / Resumo: O objetivo deste trabalho foi obter ligas amorfas em volume metálicas e magnetocalóricas
através dos processos de centrifugação e injeção. Para isto foi necessária a construção de uma injetora em vácuo de ligas metálicas. Testes para confirmar a possibilidade de obtenção de novas ligas amorfas em volume através destes processos foram feitos com composições conhecidas de ligas amorfas. A liga Fe43,6355Cr4,925Co4,925Mo12,608Mn11,032C15,563B5,8115Y1,5, conhecida como aço
amorfo estrutural, foi obtida amorfa em volume por centrifugação com espessura de 1 mm. As ligas Zr52,5Ti5Al10Cu17,9Ni14,6 e Cu55Zr30Ti10Ni5 foram obtidas amorfas em volume por injeção,
comprovando a eficiência da injetora desenvolvida no presente trabalho. A partir de uma tríade de critérios para amorfização baseada no princípio da confusão, eutéticos profundos e viscosidade elevada foram desenvolvidas novas composições de ligas. A liga Gd55Ga20Si20Ge3B2 foi obtida amorfa em volume por centrifugação e apresentou o efeito magnetocalórico tipo mesa com a maior extensão da literatura, ?T = 142 K para variação de campo magnético de 1 T, sendo também a única liga amorfa em volume magnetocalórica à base de Gd. As ligas Gd50Al23Mn23B2Ga2 e Fe43,6355Cr4,925Co4,925Ni12,608Mn11,032C15,563B5,8115Y3,0 foram composições desenvolvidas no presente trabalho que obtiveram a fase amorfa, mas não em volume, utilizando o equipamento splat-cooler. Os resultados obtidos são relevantes e indicam novos caminhos para a construção de regeneradores magnéticos e de injetoras a vácuo / Abstract: The aim of this work was to obtain metallic and magnetocaloric bulk amorphous alloys through centrifugation and injection processes. In order to obtain metallic bulk amorphous alloys a vacuum injection apparatus was built. For testing the centrifugation and injection equipments, known metallic bulk amorphous alloys were used. The alloy classified as structural amorphous steel, Fe43,6355Cr4,925Co4,925Mo12,608Mn11,032C15,563B5,8115Y1,5, was obtained in bulk amorphous by
centrifugation with a thickness of at least 1 mm. The Zr52,5Ti5Al10Cu17,9Ni14,6 and Cu55Zr30Ti10Ni5
alloys were obtained in bulk amorphous by injection. For obtaining amorphous alloys it was used
three relevant rules: confusion principle, deep eutectics, and high viscosity. The Gd55Ga20Si20Ge3B2 alloy was obtained amorphous in bulk by centrifugation and showed the largest table-like magnetocaloric effect, ?T = 142 K for a magnetic field variation of 1 T, and it is the unique based-Gd magnetocaloric bulk amorphous alloy. The Gd50Al23Mn23B2Ga2 and Fe43,6355Cr4,925Co4,925Ni12,608Mn11,032C15,563B5,8115Y3,0 alloys were developed in this work and only obtained as amorphous alloys, not in bulk, using the splat-cooler equipment. The results obtained are important and show new ways for obtaining new magnetocalric materials for magnetic
refrigerators and vacuum injection apparatus / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263194 |
Date | 15 February 2006 |
Creators | Peçanha, Rockfeller Maciel |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gama, Sergio, 1949-, Caram Junior, Rubens, 1958-, Junior, Rubens Caram, Ierardi, Maria Clara Filippini, Bertazolli, Rodnei, Coelho, Adelino de Aguiar |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 180p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0163 seconds