Previous issue date: 2004 / Resumo: A produção de concretos com elevado desempenho quanto a fluidez, propriedades reológicas e durabilidade, demanda o conhecimento das características físico-quimicas dos cimentos, intervenientes no desempenho dos mesmos. O presente trabalho estuda a influência do teor do C3A, tendo por objetivo contribuir para a compreensão dos fatores que deteiroinam o comportamento reológico das pastas de cimento. Foram selecionados três cimentos nacionais com diferentes teores de C3A e com mínimos teores de adições presentes. Efetuou-se a composição de um cimento e uma escória de alto-forao, obtendo-se também três diferentes teores de C3A. Estes materiais foram moídos em laboratório para equalização das suas áreas específicas. A avaliação do comportamento reológico embasou-se na determinação da viscosidade das pastas através de ensaios com um viscosímetro rotativo e, indiretamente, correlacionando à área de espalhamento obtida pelo ensaio do abatimento do mini-tronco de cone. O método do abatimento do mini-tronco de cone não se mostrou satisfatório para a avaliação do comportamento reológico dos materiais estudados. Através dos resultados obtidos com o viscosímetro rotativo foi possível determinar a viscosidade aparente, em função do tempo - as quais indicaram um comportamento reológico característico para as diferentes amostras e misturas avaliadas. / Abstract: The production of high performance concrete with special rheologic properties, fluidity and durability, demands the knowledge of physical and chemical characteristics of the used cement. The herein research studies the C3A influence on cement pastes, in order to add knowledge to all the aspects that can contribute to its rheologic behavior and, consequently, to mortars and concretes. It was select three Brazilian cements with different amounts of C3A and minimum additions to the clinker. It was made a composition of the cement and blast furnace granulated slag in order to obtain three different amounts of C3A. These materials were grind to have the same specific surface. The Theological behavior was studied through determination of the viscosity of the cement pastes, and correlating it with the spread surface obtained by the Kantro test. This test method was not efficient in showing the real rheologic behavior of the studied materials. It was possible to determinate the apparent viscosity with time through the use of a viscometer device, which has shown a peculiar rheological behavior to the different specimens and mixtures studied. / Mestrado / Edificações / Mestre em Engenharia Civil
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/258504 |
| Date | 17 August 2018 |
| Creators | Santos, Fabrício Bassani dos |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Paulon, Vladimir Antonio, 1938-, Silva, Vanessa Gomes da, Geyer, André Luiz Bortolacci |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Civil, Arquitetura e Urbanismo, Programa de Pós-Graduação em Engenharia Civil |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 107 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds